Process for purifying polyols made with double metal cyanide catalysts
AssigneeArco Chemical Technology, L.P.
InventorsHarry R. Hinney, Don S. Wardius
Life of this patent
Estimating the term…
Abstract
A process for purifying polyether polyols prepared using double metal cyanide (DMC) catalysts is disclosed. The process involves combining a mixture of the polyol and a C.sub.1 -C.sub.6 aliphatic alcohol with an amount of a chelating agent effective to form an insoluble complex with the catalyst, then filtering the polyol mixture to remove the insoluble complex. The process, which requires that the polyol and alcohol be present in a relative weight ratio of from 1:1 to 100:1, is effective for removing DMC residues and any cations introduced with the chelating agent.
Claims19
A process for purifying a polyether polyol prepared using a double metal cyanide catalyst, said process comprising:
- (a) combining a polyether polyol that contains double metal cyanide catalyst residues with a C.sub.1 -C.sub.6 aliphatic alcohol and a chelating agent selected from the group consisting of ethylenediaminetetraacetic acid (EDTA) and EDTA salts containing one or more cations selected from the group consisting of lithium, sodium, potassium, magnesium, calcium, ammonium, and iron, in an amount effective to form an insoluble complex with the catalyst residues;
- and
- (b) filtering the resulting mixture to remove the insoluble complex from the polyol;
- wherein the relative weight ratio of the polyether polyol to the C.sub.1 -C.sub.6 aliphatic alcohol is within the range of about 1:1 to about 100:1.
A process for purifying a polyether polyol prepared using a double metal cyanide catalyst, said process comprising:
- (a) combining a polyether polyol that contains double metal cyanide catalyst residues with an aqueous C.sub.1 -C.sub.6 aliphatic alcohol mixture and an amount of a chelating agent effective to form an insoluble complex with the catalyst residues;
- and
- (b) filtering the resulting mixture to remove the insoluble complex from the polyol;
- wherein the relative weight ratio of the polyether polyol to the aqueous C.sub.1 -C.sub.6 aliphatic alcohol mixture is within the range of about 2:1 to about 10:1, and the aqueous C.sub.1 -C.sub.6 aliphatic alcohol mixture contains from about 50 to about 95 weight percent of the aliphatic alcohol;
- and
- wherein the chelating agent is selected from the group consisting of ethylenediaminetetraacetic acid (EDTA) and EDTA salts containing one or more cations selected from the group consisting of lithium, sodium, potassium, magnesium, calcium, ammonium, and iron.
A process for purifying a polyether polyol prepared using a zinc hexacyanocobaltate catalyst, said process comprising:
- (a) combining a polyether polyol that contains zinc hexacyanocobaltate residues with aqueous isopropyl alcohol and an amount of EDTA effective to form an insoluble complex with the catalyst residues;
- and
- (b) filtering the resulting mixture to remove the insoluble complex from the polyol;
- wherein the relative weight ratio of the polyether polyol to the aqueous isopropyl alcohol is within the range of about 2:1 to about 10:1, and wherein the aqueous isopropyl alcohol contains from about 50 to about 95 weight percent of isopropyl alcohol.
Dependencies are inferred from the claim text.