Alloy powder mixture for brazing of superalloy articles

An improved braze material for brazing at least one superalloy substrate comprising:

• a high melt component having at least one metallic powder having a composition range consisting essentially of, by weight, about 4 to about 12 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities;
• and
• a eutectic component having at least one metallic powder having a composition range consisting essentially of, by weight, about 3.1 to about 8.2 percent cobalt, about 6.8 to about 38.5 percent chromium, 0 to about 12.6 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 1.3 percent molybdenum, 0 to about 23.1 percent tantalum, 0 to about 2.4 percent tungsten, 0 to about 5.1 percent niobium, 0 to about 1 percent rhenium, 0 to about 0.4 percent hafnium, 0 to about 0.6 percent yttrium, less than about 0.15 percent carbon, with the balance being nickel and incidental impurities;
• wherein the high melt component and the eutectic component together comprise a bulk composition range consisting essentially of, by weight, about 6 to about 10.2 percent cobalt, about 6 to about 16 percent chromium, about 4.5 to about 6.6 percent aluminum, 0 to about 3.5 percent titanium, 0 to about 2 percent molybdenum, about 4 to about 7.5 percent tantalum, about 3 to about 6 percent tungsten, 0 to about 2 percent niobium, 0 to about 4 percent rhenium, 0 to about 1.08 percent hafnium, 0 to about 0.2 percent yttrium, with the balance being nickel and incidental impurities;
• wherein the eutectic component comprises about 20 to about 50 percent by weight of the braze material;
• wherein the braze material has an effective brazing temperature above about 2300.degree. F.;
• wherein the high melt component is substantially solid at the effective brazing temperature;
• and
• wherein the eutectic component is substantially liquid at the effective brazing temperature.

An improved braze material for brazing at last one superalloy substrate comprising:

• a high melt component having at least one metallic powder consisting essentially of, by weight, about 4 to about 18.5 percent cobalt, about 4.5 to about 14 percent chromium, about 3 to about 6.2 percent aluminum, 0 to about 5 percent titanium, 0 to about to 4 percent molybdenum, about 3.8 to about 13.7 percent tantalum, about 4 to about 11 percent tungsten, 0 to about 0.5 percent niobium, 0 to about 12 percent rhenium, 0 to about 1.55 percent hafnium, 0 to about 0.3 percent yttrium, boron and silicon only as incidental inpurities, with the balance being nickel and other incidental impurities;
• a low melt component having at least one metallic powder consisting essentially of, by weight, about 3.9 to about 25 percent cobalt, about 4.6 to about 22 percent chromium, 0 to about 12.2 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 2 percent molybdenum, 0 to about 5.4 percent tantalum, 0 to about 7 percent tungsten, 0 to about 3 percent niobium, 0 to about 1.5 percent rhenium, 0 to about 1.1 percent hafnium, 0 to about 10 percent silicon, 0 to about 2.3 percent boron, wherein the total amount of silicon plus boron is at least 0.5 percent, with the balance being nickel and incidental impurities;
• and
• a eutectic component having at least one metallic powder having a composition range consisting essentially of, by weight, about 3.1 to about 8.2 percent cobalt, about 6.8 to about 38.5 percent chromium, 0 to about 12.6 percent aluminum, 0 to about 11.5 percent titanium, 0 to about 1.3 percent molybdenum, 0 to about 23.1 percent tantalum, 0 to about 2.4 percent tungsten, 0 to about 5.1 percent niobium, 0 to about 1 percent rhenium, 0 to about 0.4 percent hafnium, 0 to about 0.6 percent yttrium, less than about 0.15 percent carbon, with the balance being nickel and incidental impurities;
• wherein the high melt component and the low melt component and the eutectic component together comprise a bulk composition range consisting essentially of, by weight, about 6 to about 12 percent cobalt, about 7 to about 18 percent chromium, about 3 to about 6.5 percent aluminum, 0 to about 5.5 percent titanium, 0 to about 2 percent molybdenum, about 3 to about 8.5 percent tantalum, about 2.5 to about 5.5 percent tungsten, 0 to about 1.2 percent niobium, 0 to about 3.5 percent rhenium, 0 to about 1.5 percent hafnium, 0 to about 1.8 percent silicon, 0 to about 1 percent boron, 0 to about 0.1 percent carbon, with the balance being nickel and incidental impurities;
• wherein the bulk composition range comprises less than about 2.0 total weight percent of elements selected from the group consisting of boron and silicon;
• wherein the low melt component comprises about 10 to about 40 percent by weight of the braze material and the eutectic component comprises about 10 to about 30 percent by weight of the braze material;
• wherein the braze material has an effective brazing temperature above about 2300.degree. F.;
• wherein the high melt component is substantially solid at the effective brazing temperature;
• and
• wherein the low melt and eutectic components are substantially liquid at the effective brazing temperature.