US 5,238,976 AGranted
Process to enhance the tensile strength of reclaimed sand bonded with ester cured alkaline phenolic resin
AssigneeBorden, Inc.
InventorS. Raja Iyer
Life of this patent
Estimating the term…
Abstract
The present invention provides methods for treating reclaimed sand obtained from dismantled foundry molds and cores which contain a cured binder derived from an ester cured alkaline phenolic resin. Treatment of the reclaimed sand with a silane solution, particularly an aqueous solution, enhances the tensile strengths of foundry molds and cores produced therefrom beyond those obtained with untreated reclaimed sand. Methods for producing foundry cores and molds which incorporate such a treatment process are also provided by this invention as are raw batch formulations.
Claims14
A method for making a foundry shape such as a mold or a core from sand and from an alkaline phenolic resin binder that can be cured by an ester-functional curing agent, comprising
- (a) mixing together:
- (1) free-flowing granular foundry sand previously used by forming it into a resin-bonded shape using a binder of an alkaline phenolic resin cured by an ester-functional curing agent, then separated from said shape into free-flowing granules, and
- (2) pristine sand;
- (b) applying at least to said previously used sand an aqueous aminosilane solution wherein the amount of said solution is chosen to be effective to improve the tensile strength of a resin-bonded shape produced from such sand mixture over the tensile strength that would otherwise be achieved if said sand were untreated, wherein said aminosilane comprises aminoalkyl alkoxysilane which conforms to the general formula
- H.sub.2 N(CH.sub.2).sub.n Si(OR.sup.1).sub.3-x (R.sup.2).sub.x ;
- wherein n equals a whole number of from 2 to 5, R.sup.1 is an alkyl group of from 1 to 4 carbon atoms, R.sup.2 is an alkyl group of from 1 to 4 carbon atoms or phenyl, and x is 0 or 1, and an amount of an alkaline phenolic resin binder effective to bind said sand in a shape, and
- (c) effecting curing of said binder.
4 more elements
A method for making a mold or a core, or other foundry shape, from sand and an alkaline phenolic resin binder comprising placing in contact
- (a) free-flowing granular foundry and comprising sand that has been previously used by forming it into a resin-bonded shape with a binder of an alkaline phenolic resin cured by an ester-functional curing agent, then separated from said shape into free-flowing granules, and
- (b) an aqueous solution of an aminosilane, wherein said aminosilane consists:
- (1) a silane conforming to the formula
- R'Si(OR).sub.3,
- wherein R' is a C.sub.2 -C.sub.6 alkylene group bonded to an amino, hydroxy-C.sub.1 -C.sub.6 alkylamino, or amino-C.sub.1 -C.sub.6 alkylamino group, and the groups R may be the same or different and are selected from C.sub.1 -C.sub.6 alkoxy-substituted C.sub.1 -C.sub.6 alkyl groups;
- or
- (2) an aminoalkyl alkoxysilane of the formula:
- R.sub.2 N(CH.sub.2).sub.n Si(OR.sup.1).sub.3-x (R.sup.2)x
- where
- each R may be H or lower alkyl, independently of the other;
- n equals a whole number of from 2 to 4;
- R.sup.1 is an alkyl group of 2 to 4 carbons;
- R.sup.2 is lower alkyl or phenyl, and x is 0 or 1;
- or
- (3) R.sub.2 N-(CH.sub.2).sub.m -NH-(CH.sub.2).sub.n Si(OR.sup.1).sub.3-x (R.sup.2).sub.x
- where
- each R may be H or lower alkyl, independently of the other;
- m is a whole number of from 2 to 3;
- n is a whole number of from 2 to 4;
- R' is lower alkyl;
- R.sup.2 is lower alkyl, and
- x is 0 or 1;
- and
- wherein the amounts of aminosilane and water are each selected to be effective to improve the tensile strength of a resin-bonded shape produced from said granules of used sand as compared to the tensile strength that would otherwise be achieved if said used sand were not so treated, and then forming a mixture comprising:
- (i) said sand,
- (ii) a binding amount of an alkaline phenolic resin binder that can be cured at ambient temperature by a curing agent having ester-functionality, and
- (iii) an amount of a liquid curing agent that is characterized by ester-functionality, in an amount sufficient to effect cure of said binder,
- forming said mixture into a mold, core or other foundry shape, and permitting the mixture to cure in said desired shape.
25 more elements
A raw batch formulation for use in making foundry molds and cores or other foundry shapes comprising a mixture of:
- (a) a treated sand composition;
- and
- (b) an aqueous solution of a phenolic resin that can cure at ambient temperature in the presence of a curing agent having ester functionality, wherein said treated sand composition comprises an admixture of pristine sand and free-flowing granular foundry sand that has been previously used by forming it into a resin-bonded shape with a binder of an alkaline phenolic resin cured by an ester-functional curing agent, then reclaimed by being separated from said shape into free-flowing granules, after use in a metal casting process, said previously used reclaimed sand having an American Foundrymen Society's screen distribution of 25 to 140 Grain Fineness,
- said reclaimed sand being wetted with an aqueous solution of an aminosilane wherein said aminosilane comprises gamma-aminopropyl triethoxysilane,
- said solution having a concentration of from about 5% to about 90% by weight of said aminosilane, and
- said sand granules having applied thereto from about 0.05% to about 1% by weight of said solution based on the weight of the sand,
- wherein the amounts of said aminosilane and of the aqueous vehicle of said solution are each chosen to be effective to improve the tensile strength of an ester-cured, alkaline phenolic resin-bonded shape made from said treated sand, as compared to the tensile strength that would be achieved if said sand were untreated;
- wherein said pristine sand comprises at least 20% by weight of said admixture and
- wherein said aminosilane comprises gamma-aminopropyl triethoxysilane.
6 more elements
Dependencies are inferred from the claim text.