Rapid omnidirectional compaction process for producing metal nitride, carbide, or carbonitride coating on ceramic substrate
AssigneeThe Dow Chemical Company
InventorsStephen J. Doktycz, Kevin E. Howard
Life of this patent
Estimating the term…
Abstract
A process is disclosed for forming a coating on a substrate. A metal layer is placed onto the substrate either by plasma spray deposition or by applying a metal foil and then subjecting it to rapid omnidirectional compaction. The metal is then reacted with a source of carbon, nitrogen, or a combination thereof, such that a metal carbide, nitride, or carbonitride layer is formed. The product is a densified coated ceramic composition.
Claims11
A process for forming a coating on a ceramic substrate, including the steps of:
- placing a metal layer onto a surface of a ceramic substrate, where the metal is selected from tantalum, titanium, zirconium, hafnium, tungsten, molybdenum, chromium, and niobium, and where the method of placing a metal layer is comprised of placing a metal foil on the substrate and subjecting the metal layer to rapid omnidirectional compaction, such that the metal layer becomes bonded to the substrate;
- and reacting the metal layer with a source of carbon, nitrogen, or a combination thereof, where the source of carbon is a carbon-containing foil, where the carbon-containing foil is placed onto the substrate in contact with the metal layer, and where a rapid omnidirectional compaction step causes the metal layer to react with the carbon-containing foil, such that a metal carbide, nitride, or carbonitride layer is formed.
A process for forming a coating on a ceramic substrate, including the steps of:
- placing a metal foil onto a surface of a ceramic substrate, where the metal is selected from tantalum, titanium, zirconium, hafnium, tungsten, molybdenum, chromium, and niobium;
- subjecting the metal layer to rapid omnidirectional compaction, such that the metal layer becomes bonded to the substrate;
- and
- reacting the metal layer with a source of carbon, nitrogen, or a combination thereof, such that a metal carbide, nitride, or carbonitride layer is formed.
A process for forming a coating on a ceramic substrate, including the steps of:
- depositing a metal layer onto a surface of a ceramic substrate, where the metal is selected from tantalum, titanium, zirconium, hafnium, tungsten, molybdenum, chromium, and niobium, and where the depositing is done by plasma spray deposition;
- and reacting the metal layer with a source of carbon, nitrogen, or a combination thereof, where the source of carbon is a carbon-containing foil, where the carbon-containing foil is placed onto the substrate in contact with the metal layer, and where a rapid omnidirectional compaction step causes the metal layer to react with the carbon-containing foil, such that a metal carbide, nitride, or carbonitride layer is formed.