Precipitated encapsulated paper pigments and methods

A composite product consisting essentially of a substantially inert mineral nucleus selected from a group consisting of kaolinites, talcs, micas, serpertinite, montmorillonites, precipitated calcium carbonate, ground limestone, diatomaceous earth, and mixtures thereof, encapsulated with a substantially continuous uniform coating of discreet particles of an active paper pigment, substantially all of the particles having a diameter of less than one micron, the active paper pigment formed from the reagents necessary to form an alkali metal aluminosilicate, an alkali metal silicate, an alkaline earth metal aluminosilicate, and an alkaline earth metal aluminocarbonate, wherein said composite product is produced by preforming some of the active paper pigments to form a slurry under alkaline conditions, adding a slurry of mineral nucleus to the said pigment slurry and continuing formation of said active paper pigment in the presence of the mineral nucleus, always maintaining alkaline conditions.

A composite product consisting essentially of a substantially inert mineral nucleus selected from the group consisting of kaolinites, talcs, micas, serpertinite, montmorillonites, precipitated calcium carbonate, ground limestone, diatomaceous earth, and mixtures thereof at least 80% encapsulated with a substantially continuous uniform coating of discreet particles of an active paper pigment substantially all of the particles having a diameter of less than one micron selected from the group consisting of aluminocarbonates, synthetic alkali metal aluminosilicates, synthetic alkali metal silicates, synthetic alkaline earth metal aluminosilicates, and mixtures thereof, wherein said composite is produced by performing some of the paper pigment by simultaneous addition of the necessary reactants under alkaline conditions until a pigment slurry formation begins adding a slurry of mineral nucleus to the pigment slurry, and continuing simultaneous addition of the reactants to form more coating pigment in the presence of the mineral nucleus, always maintaining alkaline conditions.

A composite product comprising a substantially inert mineral nucleus selected from the group consisting of kaolinites, talcs, micas, serpertinite, montmorillonites, precipitated calcium carbonate, ground limestone, diatomaceous earth, and mixtures thereof, at least 80% encapsulated with a substantially continuous uniform coating of discreet particles of an active paper pigment substantially all of the particles having a diameter of less than one micron, said active paper pigment comprising chemically bound oxides of magnesium, sodium, aluminum and silicon, wherein the molar ratio of SiO.sub.2 to Na.sub.2 O is about 10.0 to 13.0:1, the molar ratio of Na.sub.2 O to Al.sub.2 O.sub.3 is about 0.3 to 1.0:1 and the magnesium oxide is present in an amount of from 0.1 to 8% based on the dry weight of pigment coating wherein, said pigment is produced by preforming some of the coating pigment to form a slurry of coating pigment under alkaline conditions, adding a slurry of mineral nucleus to the alkaline pigment slurry, and then continuing formation of said coating pigment in the presence of the mineral nucleus, always maintaining alkaline conditions.