Phenolic resin coated proppants with reduced hydraulic fluid interaction
AssigneeBorden, Inc.
InventorsCalvin R. Johnson, Kwok-tuen Tse, Charles J. Korpics
Life of this patent
Estimating the term…
Abstract
The invention relates to the modification of a curable phenolic resin system by the incorporation of alkylphenol, alkoxyphenol, arylphenol or aryloxyphenol. The resulting resin has reduced water soluble leachates which, in turn, improves the break time when the resin is used to coat proppants for treating subterranean formations.
Claims25
A curable phenolic resin composition useful as a subterranean proppant coating comprising:
- (a) a novolak resin;
- and
- (b) a resole resin, wherein at least one of the resins is modified by the incorporation of a phenolic material selected from the group consisting of arylphenol, alkylphenol, alkoxyphenol, and aryloxyphenol and wherein the weight ratio of novolak resin to resole resin is from about 4:1 to about 1:9, and wherein the content of the modifying phenolic material is sufficient to reduce the water solubility of the coating relative to a comparable mixture of novolak and resole resins which is not modified and wherein the composition does not contain sufficient hexamethylenetetramine to effect the cure of the composition.
A method of preparing a phenolic resin-coated sand comprising:
- (a) combining alkylphenol and phenol in a molar ratio of 0.05:1 to 0.60:1;
- (b) reacting phenol or the combination from (a) with a source of formaldehyde in a phenol:formaldehyde ratio of from about 1:1 to about 4:1 under basic conditions sufficient to produce a resole or an alkylphenol-modified resole resin;
- (c) combining the resin from step (b) with sand heated to a temperature above 250.degree. F. for a time sufficient to allow the resin to increase in molecular weight;
- (d) adding a novolac resin to the mixture in (c), wherein the weight ratio of novolak resin to resole resin is from about 4:1 to about 1:9 on a solids basis, whereby the sand becomes coated;
- (e) adding sufficient water to quench the reaction;
- (f) cooling the resulting phenolic resin-coated sand.
3 more elements
A method of preparing phenolic resin-coated sand comprising:
- (a) adding a novolak resin to sand heated to a temperature above 250.degree. F.;
- (b) adding to the stirring mixture from (a) phenol or an alkylphenol-modified, alkoxyphenol-modified, aryloxyphenol-modified, or arylphenol-modified resole resin prepared by reacting a mixture comprising an alkylphenol, alkoxyphenol, aryloxyphenol or arylphenol with a molar excess of formaldehyde under alkaline conditions sufficient to produce a resole resin, whereby the sand is coated;
- (c) adding sufficient water to quench the reaction;
- and
- (d) cooling the resulting phenolic resin-coated sand.
2 more elements
An improved method for treating subterranean formations comprising:
- (a) applying to a subterranean formation a proppant coated with a curable phenolic coating composition, wherein the phenolic coating composition comprises a mixture of a novolak resin and a resole resin, wherein the spectrophotometric absorbance at 510 mu of the water soluble leachate from the phenolic coated sand composition is below about 1.68, and wherein the phenolic coating composition does not comprise hexamethylenetetramine in an amount sufficient to significantly affect subsequent cure of the coating composition;
- and
- (b) curing the curable phenolic coating composition by exposing the coating composition to sufficient heat and pressure in the subterranean formation to cause crosslinking of the resins, and consolidation of the proppant, whereby a cured proppant coating with reduced water solubility is attained.
A curable phenolic resin composition useful as a subterranean proppant coating comprising:
- (a) a novolak resin;
- and
- (b) a resole resin,
- and wherein the weight ratio of novolak resin to resole resin is from about 4:1 to about 1:9, and wherein the molecular weight of the resin composition is sufficiently advanced to reduce the water solubility of the coating relative to a comparable mixture of novolak and resole resins which is not similarly advanced, and wherein the composition does not contain sufficient hexamethylenetetramine to effect the cure of the composition.