AssigneeMartin Marietta Corporation
InventorsJoseph R. Pickens, Timothy J. Langan, Frank H. Heubaum, Lawrence S. Kramer, Alex Cho
Estimating the term…
Aluminum-base alloys containing Cu, Li, Zn, Mg and Ag are disclosed which possess highly desirable properties, such as relatively low density, high modulus, high strength/ductility combinations, strong natural aging response with and without prior cold work, and high artificially aged strength with and without prior cold work. In addition, the alloys possess good weldability, corrosion resistance, cryogenic properties, and elevated temperature properties. The alloys may comprise from about 1 to about 7 weight percent Cu, from about 0.1 to about 4 weight percent Li, from about 0.01 to about 4 weight percent Zn, from about 0.05 to about 3 weight percent Mg, from about 0.01 to about 2 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from Zr, Cr, Mn, Ti, Hf, V, Nb, B and TiB.sub.2, and the balance Al along with incidental impurities. Preferred alloys comprise from about 3.0-6.5 weight percent Cu, from about 0.5-2.6 weight percent Li, from about 0.05-2 weight percent Zn, from about 0.1-1.5 weight percent Mg, from about 0.05-1 weight percent Ag, from about 0.05-0.5 weight percent grain refiner, and the balance Al and incidental impurities. Additional elements selected from Ge, Sn, Cd, In, Be, Sr, Sc, Y, and Ca may be used in addition to, or in place of, Zn in the present alloys.
An aluminum-base alloy consisting essentially of from about 1 to about 7 weight percent Cu, from about 0.1 to about 4 weight percent Li, from about 0.5 to about 4 weight percent total of at least one element selected from the group consisting of Zn, Ge, Sn, Cd, In, Be, Sr, Sc, Y, and Ca, from about 0.05 to about 3 weight percent Mg, from about 0.01 to about 2 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
An aluminum-base alloy consisting essentially of from about to about 7 weight percent Cu, from about 0.1 to about 4 weight percent Li, from about 0.5 to about 4 weight percent Zn, from about 0.05 to about 3 weight percent Mg, from about 0.01 to about 2 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
An aluminum-base alloy consisting essentially of from about 3.0 to about 6.5 weight percent Cu, from about 0.5 to about 2.6 weight percent Li, from about 0.5 to about 2 weight percent Zn, from about 0.1 to about 1.5 weight percent Mg, from about 0.05 to about 1 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
An aluminum-base alloy consisting essentially of from about 3.5 to about 5.5 weight percent Cu, from about 0.8 to about 2.0 weight percent Li, from about 0.5 to about 1.5 weight percent Zn, from about 0.2 to about 0.8 weight percent Mg, from about 0.1 to about 0.5 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
An aluminum-base alloy consisting essentially of from about 4.0 to about 5.0 weight percent Cu, from about 1.0 to about 1.6 weight percent Li, from about 0.5 to about 0.75 weight percent Zn, from about 0.3 to about 0.5 weight percent Mg, from about 0.1 to about 0.4 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
A cryogenic aluminum-base alloy consisting essentially of from about 3.0 to about 6.5 weight percent Cu, from about 0.5 to about 2.6 weight percent Li, from about 0.5 to about 2 weight percent Zn, from about 0.1 to about 1.5 weight percent Mg, from about 0.05 to about 1 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
A weldable aluminum-base alloy consisting essentially of from about 4.0 to about 6.5 weight percent Cu, from about 0.8 to about 2.0 weight percent Li, from about 0.5 to about 1.5 weight percent Zn, from about 0.2 to about 0.8 weight percent Mg, from about 0.1 to about 0.5 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
A cold worked, naturally aged aluminum-base alloy consisting essentially of from about 4.0 to about 5.5 weight percent Cu, from about 0.9 to about 1.6 weight percent Li, from about 0.5 to about 1 weight percent Zn, from about 0.2 to about 0.5 weight percent Mg, from about 0.1 to about 0.5 weight percent Ag, from about 0.05 to about 0.5 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2, and mixtures thereof, and the balance aluminum and incidental impurities, which in the T3 temper possesses a yield strength in the range of from about 50 to about 75 ksi, an ultimate tensile strength in the range of from about 65 to about 88 ksi, and an elongation in the range of from about 8 to about 25 percent.
A non-cold worked, naturally aged aluminum-base alloy consisting essentially of from about 4.0 to about 5.5 weight percent Cu, from about 0.9 to about 1.6 weight percent Li, from about 0.5 to about 1 weight percent Zn, from about 0.2 to about 0.5 weight percent Mg, from about 0.1 to about 0.5 weight percent Ag, from about 0.05 to about 0.5 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2, and mixtures thereof, and the balance aluminum and incidental impurities, which in the T4 temper possesses a yield strength in the range of from about 55 to about 77 ksi, an ultimate tensile strength in the range of from about 67 to about 100 ksi, and an elongation in the range of from about 8 to about 25 percent.
A non-cold worked, artificially aged aluminum-base alloy consisting essentially of from about 4.0 to about 5.5 weight percent Cu, from about 0.9 to about 1.6 weight percent Li, from about 0.5 to about 1 weight percent Zn, from about 0.2 to about 0.5 weight percent Mg, from about 0.1 to about 0.5 weight percent Ag, from about 0.05 to about 0.5 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2, and mixtures thereof, and the balance aluminum and incidental impurities, which in the T6 temper possesses a yield strength in the range of from about 70 to about 110 ksi, an ultimate tensile strength in the range of from about 80 to about 118 ksi, and an elongation in the range of from about 1 to about 10 percent.
A cold worked, artificially aged aluminum-base alloy consisting essentially of from about 4.0 to about 5.5 weight percent Cu, from about 0.9 to about 1.6 weight percent Li, from about 0.5 to about 1 weight percent Zn, from about 0.2 to about 0.5 weight percent Mg, from about 0.1 to about 0.5 weight percent Ag, from about 0.05 to about 0.5 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2, and mixtures thereof, and the balance aluminum and incidental impurities, which in the T8 temper possesses a yield strength in the range of from about 70 to about 110 ksi, an ultimate tensile strength in the range of from about 80 to about 118 ksi, and an elongation in the range of from about 2 to about 15 percent.
A welding filler alloy for welding aluminum-base alloys, the welding alloy consisting essentially of from about 4.0 to about 6.5 weight percent Cu, from about 0.5 to about 2.6 weight percent Li, from about 0.5 to about 2 weight percent Zn, from about 0.05 to about 0.8 weight percent Mg, from about 0.1 to about 1 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities.
An aluminum-base alloy consisting essentially of from about 3.0 to about 6.5 weight percent Cu, from about 0.5 to about 2.6 weight percent Li, from about 0.5 to about 2 weight percent Zn, from about 0.1 to about 1.5 weight percent Mg, from about 0.05 to about 1 weight percent Ag, from about 0.01 to about 2 weight percent grain refiner selected from the group consisting of Zr, Cr, Mn, Ti, Hf, V, Nb, B, TiB.sub.2 and combinations thereof, and the balance aluminum and incidental impurities, wherein the weight percent ratio of Cu to Li is greater than about 2.5.
An aluminum-base alloy consisting essentially of about 4.75 weight percent Cu, about 1.3 weight percent Li, from about 0.5 to about 2.0 weight percent Zn, about 0.4 weight percent Mg, about 0.4 weight percent Ag, about 0.14 weight percent Zr, and the balance aluminum and incidental impurities.
Dependencies are inferred from the claim text.