Manufacture of sintered uranium dioxide
AssigneeBritish Nuclear Fuels plc
InventorGeoffrey A. Wood
Life of this patent
Estimating the term…
Abstract
A method of manufacturing sintered uranium dioxide in which a mixture is formed of single crystals of uranium dioxide and uranium dioxide powder. Compacts are formed from granules of the mixture, the compacts are sintered in carbon dioxide, and then reduced in a hydrogen environment at a substantially lower temperature than the sintering temperature. The quantity of the single crystals is selected so as to inhibit excessive grain growth in the compacts during sintering.
Claims13
A method of manufacturing sintered uranium dioxide pellets having a substantially uniform microstructure, the method including the steps of forming a mixture of a predetermined quantity of seeds comprising single crystals of uranium dioxide with a powder comprising uranium dioxide, producing granules from the mixture, forming compacts comprising the granules, sintering the compacts at a first temperature in a gaseous environment consisting essentially of carbon dioxide, and then subjecting the compacts to a reducing gaseous environment comprising hydrogen at a substantially lower temperature than the first temperature, the quantity of seeds being such, and the size range of the seeds being restricted so, as to stabilise the microstructure of the sintered compacts by inhibiting excessive grain growth in the compacts during said sintering step.
A method of manufacturing sintered uranium dioxide pellets having a substantially uniform microstructure, the method including the steps of forming a mixture of a predetermined quantity of seeds comprising single crystals of uranium dioxide with a powder comprising uranium dioxide, producing granules from the mixture, forming compacts comprising the granules, sintering the compacts at a first temperature in a gaseous environment consisting essentially of carbon dioxide, and then subjecting the compacts to a reducing gaseous environment comprising hydrogen at a substantially lower temperature than the first temperature, the quantity of seeds being such as to stabilise the microstructure of the sintered compacts by inhibiting excessive grain growth in the compacts during said sintering step, the sintering step being performed at a temperature of about 1700.degree. C., and the reducing step being performed at a temperature of about 1150.degree. C., at heating and cooling rates of about 10.degree. C. per minute between ambient and 1700.degree. C. and on cooling from 1700.degree. C. to 1150.degree. C.
A method for the manufacture of sintered uranium dioxide pellets having a substantially uniform microstructure, the method comprising:
- (a) manufacturing a preselected quantity of seeds comprising single crystals of uranium dioxide of a size not exceeding 38 microns;
- (b) mixing the seeds in a quantity of about 2% by weight with a powder comprising uranium dioxide and homogenising the mixture;
- (c) granulating and pelleting the mixture;
- (d) pressing the resultant pellets;
- (e) sintering the pellets in a gaseous environment consisting essentially of carbon dioxide for a period of about 5 hours at a temperature of about 1700.degree. C. at a heating rate between ambient and said 1700.degree. C. of about 10.degree. C. per minute, and
- (f) subjecting the sintered pellets for a period of about 1 hour to a reducing gaseous environment comprising hydrogen at a temperature of about 1150.degree. C. at a cooling rate between said 1700.degree. and 1150.degree. C. of about 10.degree. C. per minute.