Zirconium alloy with superior ductility
AssigneeCombustion Engineering, Inc.
InventorsAnand M. Garde, Satya R. Pati
Life of this patent
Estimating the term…
Abstract
A stabilized alpha metal matrix provides an improved ductility, creep strength, and corrosion resistance under neutron irradiation environment in a zirconium alloy containing tin in a range of 0.8 to 1.2 percent; iron in a range of 0.2 to 0.5 percent, and typically 0.35 percent; chromium in a range of 0.1 to 0.4 percent, and typically 0.25 percent; niobium in a range of from a measurable amount up to 0.6 percent, and typically 0.30 percent; silicon in a range of 50 to 200 ppm, and typically 100 ppm; and oxygen in a range 900 to 1800 ppm, typically 1600 ppm. The silicon is added as an alloying element to reduce hydrogen absorption by the alloy and to reduce variations in the corrosion resistance with variations in the processing history of the alloy.
Claims22
An improved ductile modified zirconium alloy for use in light water nuclear core structural elements in fuel cladding, which comprises:
- measurable amounts of alloying material from the group including niobium or molybdenum, or combinations thereof, niobium being present in a range of from a measurable amount up to 0.6 percent by weight, said alloying material homogeneously dissolved in alpha Zircaloy with 0.8 to 1.2 percent by weight tin, 0.2 to 0.5 percent by weight iron, 0.1 to 0.4 percent by weight chromium, silicon in the range of 50 to 200 ppm, and oxygen in the range of 900 to 1800 ppm.
A zirconium alloy for use in light water nuclear core structure elements in fuel cladding, which comprises a composition as follows:
- tin, in a range of 0.8 to 1.2 percent;
- iron, in a range of 0.2 to 0.5 percent;
- chromium, in a range of 0.1 to 0.4 percent;
- niobium, in a range of from a measurable amount up to 0.6 percent;
- silicon, in a range of 50 to 200 ppm;
- and
- oxygen, in a range of 900 to 1800 ppm.
A method of making a zirconium alloy, comprising the steps of:
- providing a zirconium-alloy having tin in a range of about 0.8 to 1.2 percent;
- iron in a range of 0.2 to 0.5 percent;
- chromium in a range of 0.1 to 0.4 percent;
- niobium in a range of from a measurable amount to 0.6 percent;
- and an oxygen in a range of 900 to 1800 ppm;
- and
- adding silicon in a range of 50 to 200 ppm as an alloying element to reduce the hydrogen absorption by the alloy and to reduce the variation of the corrosion resistance with variations in the processing history of the alloy.
Dependencies are inferred from the claim text.