Preparation method of high purity 115 K Tl-based superconductor
AssigneeIndustrial Technology Research Institute
InventorsChung-Kwang Chiang, Cheng-Yie Shei
Life of this patent
Estimating the term…
Abstract
A preparation method for high-purity Tl-based superconductor phase of 115 K, and the precursor thereof. The process comprises a specific composition of precursors, represented by the formula: (Tl.sub.a Pb.sub.b Bi.sub.c)Sr.sub.2-x Ca.sub.2+x Cu.sub.y O.sub.z, wherein (a+b+c)=1, 0<x.ltoreq.1 and 2.ltoreq.y.ltoreq.4, for the manufacturing of Tl-based superconductor by adding oxalic acid as a chelating agent which equals to half the molar amount of total nitrate anions in the required metal nitrates aqueous solution and adjusting pH value of the solution to obtain the superconductor.
Claims5
A preparation method of high purity 115K Tl-based superconductor comprising the steps of:
- (a) preparing an aqueous solution of thallium (+3) oxide and metal nitrates of Bi, Pb, Sr, Ca and Cu in composition ratio of (Tl.sub.a Pb.sub.b Bi.sub.c)Sr.sub.2-x Ca.sub.2+x Cu.sub.y O.sub.z, wherein (a+b+c)=1, 0.55.ltoreq.a.ltoreq.0.65, 0.15.ltoreq.b.ltoreq.0.25, 0.15.ltoreq.c.ltoreq.0.25, 0<x.ltoreq.1 and 2.ltoreq.y.ltoreq.4;
- (b) adding oxalic acid as a chelating agent into the prepared aqueous solution, which equals half the molar amount of total nitrate anions;
- (c) adjusting pH=5-8 of the solution containing metal salts and chelating acid by adding ammonia water, ethylenediamine or triethylamine;
- (d) stirring vigorously and heating the solution to a temperature of about 100.degree. to about 120.degree. C. to form a gel;
- (e) heating the obtained gel of step (d) for organic decomposition at 200.degree.-750.degree. C. to form precursors in flaky shapes, then grinding to fine precursor powders;
- and
- (f) calcinating and sintering the precursor powders to obtain the superconductor product.
Dependencies are inferred from the claim text.