US 5,208,310 AGranted

Method for preparation of very high molecular weight polycarborane siloxanes

AssigneeHughes Aircraft Company

InventorThomas K. Dougherty

Life of this patent

Estimating the term…

Loading patent…

Abstract

An improved method for the preparation of very high molecular weight polycarborane siloxane polymers in which each of the reactants is first provided in an ultra-pure state by a series of recrystallization procedures in specific solvents. The reactants are then reacted in the following series of steps by: (a) providing ultra-pure carborane bisdimethyl silanol in dried chlorobenzene solvent, to form a slurry and cooling said slurry to -10.degree..+-.5.degree. C.; (b) adding to said slurry a mixture of ultra-pure dimethylbisureido silane and ultra-pure methylphenylbisureido silane to form a reaction mixture at -10.degree..+-.5.degree. C.; (c) separating from said reaction mixture a silanol end-capped prepolymer of said polycarborane siloxane polymer; (d) dissolving said prepolymer in chlorobenzene to form a solution; and (e) adding to said prepolymer solution an excess of said ultra-pure bisureido silane selected from the group consisting of dimethylbisureido silane, methylphenylbisureido silane and a mixture thereof, to form said very high molecular weight polycarborane siloxane polymer. Alternatively, step (e) may be performed at 60.degree.-70.degree. C. to further increase the molecular weight of the polymer. In an alternative process, step (b) is performed at -15.degree. to -20.degree. C. for 6 to 20 hours and steps (c) through (e) are omitted.

Claims3

Dependent claims

In a method for the preparation of a very high molecular weight polycarborane siloxane polymer comprising the step of:

(a) providing carborane bisdimethyl silanol in dried chlorobenzene solvent, to form a slurry and cooling said slurry to -10.degree..+-.5.degree. C.;
(b) adding to said slurry a mixture of dimethylbisureido silane and methylphenylbisureido silane to form a reaction mixture at -10.degree..+-.5.degree. C.;
(c) separating from said reaction mixture a silanol end-capped prepolymer of said polycarborane siloxane polymer;
(d) dissolving said prepolymer in chlorobenzene to form a solution;
and
(e) adding to said prepolymer solution an excess of said bisuriedo silane selected from the group consisting of dimethylbisureido silane, methylphenylbisureido silane and a mixture thereof to form said very high molecular weight polycarborane siloxane polymer, wherein the improvement comprises:
(i) providing said carborane bisdimethyl silanol in an ultra-pure state by dissolving said carborane bisdimethylsilanol in a dry, oxygen-free mixture of hexane and toluene by heating to approximately 70.degree. C. in an inert atmosphere to form a first solution, filtering said first solution and cooling said first filtered solution to form a first crystalline product, and repeating said dissolving of said first crystalline product, said filtering, and said cooling for a total of 2 to 5 additional times;
(ii) providing said dimethylbisureido silane in an ultra-pure state by dissolving said dimethylbisureido silane in a dry, oxygen-free mixture of diisopropyl ether and tetrahydrofuran by heating to approximately 60.degree. C. in an inert atmosphere to form a second solution, filtering said second solution, and cooling said second filtered solution to form a second crystalline product, and repeating said dissolving of said second crystalline product, said filtering, and cooling one time;
and
(iii) providing said methylphenylbisureido silane in an ultra-pure state by dissolving said methylphenylbisureido silane in dry, oxygen-free diisopropyl ether by heating to form a third solution, filtering said third solution, adding dry hexane to said third filtered solution to form a mixture and cooling said mixture to room temperature, to form a third crystalline product and repeating said dissolving of said third crystalline product, said filtering, said adding of hexane and said cooling two additional times;
whereby said polycarborane siloxane polymer has a molecular weight in excess of 120,000.

8 more elements

A method for preparation of a very high molecular weight polycarborane siloxane polymer comprising the steps of:

(a) providing carborane bisdimethyl silanol in an ultra-pure state by dissolving said carborane bisdimethylsilanol in a dry, oxygen-free mixture of hexane and toluene by heating to approximately 70.degree. C. in an inert atmosphere to form a first solution, filtering said first solution, and cooling said first filtered solution to form a first crystalline product, and repeating said dissolving of said first crystalline product, said filtering, and said cooling for a total of 2 to 5 additional times;
(b) providing dimethylbisureido silane in an ultra-pure state by dissolving said dimethylbisureido silane in a dry, oxygen-free mixture of diisopropyl ether and tetrahydrofuran by heating to approximately 60.degree. C. in an inert atmosphere to form a second solution, filtering said second solution, and cooling said second filtered solution to form a second crystalline product, and repeating said dissolving of said second crystalline product, said filtering, and said cooling one time;
and
(c) providing methylphenylbisureido silane in an ultra-pure state by dissolving said methylphenylbisureido silane in dry, oxygen-free diisopropyl ether by heating to form a third solution, filtering said third solution, adding dry hexane to said third filtered solution to form a mixture and cooling said mixture to room temperature, to form a third crystalline product and repeating said dissolving of said third crystalline product, said filtering, said adding of hexane and said cooling two additional times;
(d) mixing said ultra-pure carborane bisdimethylsilanol in dried chlorobenzene solvent to form a slurry and cooling said slurry to -15.degree..+-.5.degree. C.;
and
(e) adding to said slurry a predetermined amount of said ultra-pure dimethylbisureido silane and said ultra-pure methylphenylbisureido silane to form a reaction mixture and maintaining said reaction mixture at a temperature within the range of -15.degree. to -20.degree. C. for 6 to 20 hours, whereby said very high molecular weight polycarborane siloxane polymer is formed having a molecular weight in excess of 300,000.

4 more elements