Process for fabricating flexible BI-PB-SR-CA-CU-O superconducting tape
AssigneeIndustrial Technology Research Institute
InventorsKouth Chen, Lian-Haei Horng, Horng-Show Koo, Weir-Mirn Hurng, Wun-Hsin Lee
Life of this patent
Estimating the term…
Abstract
A superconducting tape is fabricated with a composition of Bi.sub.1.81 Pb.sub.0.43 Sr.sub.1.71 Ca.sub.2.14 Cu.sub.3 O.sub.x. The powder of composition is filled into a silver tube and the silver tube is processed by rolling or pressing into a thin tape. The thin tape is heat treated and pressed for several times until the superconducting phase is formed to the tape and the thickness of the tape is equal to or less than 0.07 mm. The resulting tape is highly flexible such that it can be bent into an arc with a very small radius of curvature and nonetheless provide high critical current density.
Claims2
A process for fabricating a superconducting tape, comprising:
- (a) preparing a Bi.sub.1.81 Pb.sub.0.43 Sr.sub.1.71 Ca.sub.2.14 Cu.sub.3 O.sub.x superconducting composition;
- (b) filling a silver tube with the superconducting composition;
- (c) gradually forming, from the filled silver tube, a tape with a thickness equal to or less than 0.07 mm through a series of at least two pressing steps, each pressing step being followed by a heat-treatment process which comprises raising gradually the temperature of the pressed tape from a room temperature of about 25.degree. C. to an elevated temperature of about 843.degree. C., maintaining the tape at the elevated temperature of about 843.degree. C. for a period of about 24 to 48 hours, and decreasing gradually the elevated temperature to the room temperature.
Dependencies are inferred from the claim text.