Microporous alumina ceramic membranes
AssigneeWisconsin Alumni Research Foundation
InventorsMarc A. Anderson, Guangyao Sheng
Life of this patent
Estimating the term…
Abstract
Several methods are disclosed for the preparation microporous alumina ceramic membranes. For the first time, porous alumina membranes are made which have mean pore sizes less than 100 Angstroms and substantially no pores larger than that size. The methods are based on improved sol-gel techniques.
Claims11
A method of making microporous alumina ceramic membranes comprising the steps of
- (a) introducing an aluminum alkoxide into aqueous solution;
- (b) peptizing the solution by the addition of acid at a temperature less than 80.degree. C. under conditions that favor the formation of small alumina particles in the solution;
- (c) recovering from the solution a stable sol;
- (d) removing solvent from the sol to form a xerogel;
- and
- (e) firing the xerogel at temperatures up to 500.degree. C. to obtain a porous ceramic alumina membrane having a narrow distribution of pore sizes.
A method of making microporous alumina ceramic membranes comprising the steps of
- (a) introducing an aluminum alkoxide into aqueous solution;
- (b) peptizing the solution by the addition of acid at a temperature less than 80.degree. C. under conditions that favor the formation of small alumina particles in the solution;
- (c) heating the solution to over 80.degree. C. to induce formation of boehmite particles in the solution;
- (d) removing solvent from the solution to form a xerogel;
- and
- (e) firing the xerogel at temperatures up to 500.degree. C. to obtain a porous ceramic alumina membrane having a narrow distribution of pore sizes.
A method of making microporous alumina ceramic membranes comprising the steps of
- (a) introducing an aluminum alkoxide into aqueous solution;
- (b) peptizing the solution by the addition of acid at a temperature less than 80.degree. C. under dilute conditions that inhibit the formation of large alumina particles in the solution;
- (c) concentrating the particle in the solution to form a stable alumina sol;
- (d) removing solvent from the sol to form a xerogel;
- and
- (e) firing the xerogel at temperatures up to 500.degree. C. to obtain a porous ceramic alumina membrane having a narrow distribution of pore sizes.
A method of making microporous alumina ceramic membranes comprising the steps of
- (a) introducing an aluminum alkoxide into alcoholic solution with a limited amount of water;
- (b) peptizing the solution by the addition of acid at a temperature less than 80.degree. C. under conditions that favor the formation of small particles in the solution;
- (c) aging the solution until a stable sol is formed;
- (d) removing solvent from the sol to form a xerogel;
- and
- (e) firing the xerogel at temperatures up to 500.degree. C. to obtain a porous ceramic alumina membrane having a narrow distribution of pore sizes.
A microporous alumina ceramic membrane, the membrane having a specific surface area in excess of 100 square meters per gram and a mean pore size of less than 100 Angstroms and being substantially free of pores having a radius in excess of 100 Angstroms.
Dependencies are inferred from the claim text.