Synthesis of a crystalline silicoaluminophosphate
AssigneeChevron Research and Technology Company
InventorStephen J. Miller
Life of this patent
Estimating the term…
Abstract
A method is disclosed for preparing a silicoaluminophosphate molecular sieve, characterized in that the P.sub.2 O.sub.5 to alumina mole ratio at the surface is about 0.80 or less, the P.sub.2 O.sub.5 to alumina mole ratio of the bulk is 0.96 or greater and the silicon content at the surface is greater than that of the bulk, from a reaction mixture containing particles less than 80 microns in diameter.
Claims17
A process for preparing a crystalline silicoaluminophosphate molecular sieve having a characteristic X-ray powder diffraction pattern which contains at least the d-spacings of Table I, and wherein the P.sub.2 O.sub.5 to alumina mole ratio at the surface of the silicoaluminophosphate is about 0.80 or less, the P.sub.2 O.sub.5 to alumina mole ratio of the bulk of the silicoaluminophosphate is 0.96 or greater, and the SiO.sub.2 to alumina mole ratio at the surface is greater than in the bulk of the silicoaluminophosphate, said process comprising:
- a. preparing an aqueous reaction mixture containing a reactive source of SiO.sub.2, aluminum isopropoxide, phosphoric acid, and an organic templating agent, said reaction mixture having at least 80 weight percent of the particles of size less than 80 microns in diameter, and said reaction mixture having a composition expressed in terms of mole ratios of oxides of:
- aR:Al.sub.2 O.sub.3 :0.9-1.2P.sub.2 O.sub.5 :0.1-4.0SiO.sub.2 :bH.sub.2 O
- wherein R is an organic templating agent;
- "a" has a value large enough to constitute an effective amount of R;
- "b" has a value such that there are 10 to 40 moles of H.sub.2 O per mole of aluminum oxide;
- said reaction mixture having been formed by combining the alumina and phosphorus sources in the substantial absence of the silicon source, thereafter combining the resulting mixture with the
- silicon source and the organic templating agent to form the complete reaction mixture;
- b. insuring the pH of the reaction mixture is from about 6.0 to 8.5;
- c. heating the reaction mixture to a temperature in the range of from 150.degree. C. to 240.degree. C. until crystals of silicoaluminophosphate are formed;
- and
- d. recovering said crystals.
A process for preparing a crystalline silicoaluminophosphate molecular sieve having a characteristic X-ray powder diffraction pattern which contains at least the d-spacings of Table I, and wherein the P.sub.2 O.sub.5 to alumina mole ratio at the surface of the silicoaluminophosphate is about 0.80 or less, the P.sub.2 O.sub.5 to alumina mole ratio of the bulk of the silicoaluminophosphate is 0.96 or greater, and the SiO.sub.2 to alumina mole ratio at the surface is greater than in the bulk of the silicoaluminophosphate, said process comprising:
- a. homogenizing an aqueous reaction mixture containing aluminum isopropoxide and phosphoric acid under conditions such that at least 80 weight percent of the particles in said reaction mixture are reduced in size to less than 80 microns in diameter;
- b. adding to the homogenized reaction mixture a reactive source of SiO.sub.2 and an organ agent to give a combined reaction mixture having a composition expressed in terms of mole ratios of oxides of:
- aR:Al.sub.2 O.sub.3 :0.09-1.2P.sub.2 O.sub.5 :0.1-4.0SiO.sub.2 :bH.sub.2 O
- wherein "R" is an organic templating agent;
- "a" has a value large enough to constitute an effective amount of R;
- "b" has a value such that there are 10 to 40 moles of H.sub.2 O per mole of aluminum oxide;
- said reaction mixture having been formed by combining the alumina and phosphorus sources in the substantial absence of the silicon source, thereafter combining the resulting mixture with the silicon source and the organic templating agent to form the complete reaction mixture;
- c. insuring the pH of the reaction mixture is from about 6.0 to 8.5;
- d. heating the reaction mixture to a temperature in the range of from 150.degree. C. to 240.degree. C. until crystals of silicoaluminophosphate are formed;
- and
- e. recovering said crystals.
A process for preparing a crystalline silicoaluminophosphate molecular sieve having a composition in terms of mole ratios of oxides on an anhydrous basis expressed by the formula:
- mR:Al.sub.2 O.sub.3 :nP.sub.2 O.sub.5 :qSiO.sub.2
- wherein "R" represents at least one organic templating agent present in the intracrystalline pore system;
- "m" represents the moles of "R" present and has a value such that there are from 0.02 to 2 moles of R per mole of aluminum;
- n has a value of from 0.96 to 1.1, and q has a value of from 0.1 to 4, said silicoaluminophosphate having a characteristic X-ray powder diffraction pattern which contains at least the d-spacings of Table I, and wherein the P.sub.2 O.sub.5 to alumina mole ratio of the surface of the silicoaluminophosphate is about 0.80 or less, the P.sub.2 O.sub.5 to alumina mole ratio of the bulk of the silicoaluminophosphate is greater than the SiO.sub.2 to alumina mole ratio in the bulk of the silicoaluminophosphate, which process comprises:
- a. homogenizing an aqueous reaction mixture containing aluminum isopropoxide and phosphoric acid under conditions such that at least 80 weight percent of the particles in said reaction mixture are reduced in size to less than 80 microns in diameter;
- b. adding to the homogenized reaction mixture a reactive source of SiO.sub.2 and an organic templating agent to give a combined reaction mixture having a composition expressed in terms of mole ratios of oxides of:
- aR:Al.sub.2 O.sub.3 :0.9-1.2P.sub.2 O.sub.5 :0.1-4.0SiO.sub.2 :bH.sub.2 O
- wherein "R" is an organic templating agent;
- "a" has a value large enough to constitute an effective amount of R;
- "b" has a value such that there are 10 to 40 moles of H.sub.2 O per mole of aluminum oxide;
- said reaction mixture having been formed by combining the alumina and phosphorus sources in the substantial absence of the silicon source, thereafter combining the resulting mixture with the silicon source and the organic templating agent to form the complete reaction mixture;
- c. insuring the pH of the reaction mixture is from about 6.0 to 8.5;
- d. heating the reaction mixture to a temperature in the range of from 150.degree. C. to 240.degree. C. until crystals of silicoaluminophosphate are formed;
- and
- e. recovering said crystals.