US 5,207,956 A · Computer-controlled method for composite curing

Abstract

The present invention comprises a method for controlling the curing process of a composite material part in a curing vessel such as an autoclave. The method relies on the comparison of actual part parameter values to predicted part parameter values wherein the predicted values are obtained from computer simulations of the cure cycles using thermo-chemical, cure kinetics, resin flow and viscosity analytic models. The invention provides a methodology for the continuous selection and updating during the cure process of new optimal cure cycles from sets of cure cycles in response to actual material behavior during the curing process.

Claims18

Dependent claims

A method for controlling a curing process for curing a composite material part in a curing vessel, comprising the steps of:

placing the composite material part in the curing vessel;
selecting an initial cure cycle;
beginning the curing process of the composite material part in accordance with the initial cure cycle;
measuring an actual part temperature of the part during the curing process;
measuring a pressure within the curing vessel during the curing process;
directly measuring during the curing process at least one additional real part parameter value;
comparing the additional real part parameter value to a predicted part parameter value determined from a predictive analytic model;
selecting a new cure cycle periodically during the curing process when the additional real part parameter value falls outside of a predetermined acceptable range about the predicted part parameter value;
and
adjusting the curing process in accordance with the new cure cycle.

7 more elements

A method for controlling a curing process of a composite material part in a curing vessel, the part having at least one ply, the method comprising the steps of:

(a) providing an analytic model for calculating a predicted temperature of the part predicted to occur at a predetermined time during the curing process;
(b) measuring an actual maximum temperature of the part at the predetermined time during the curing process;
(c) comparing the predicted temperature to the actual maximum temperature;
(d) selecting a new cure cycle when the actual maximum temperature falls outside of an acceptable temperature range about the predicted temperature;
(e) adjusting an ambient temperature in the curing vessel in accordance with the new cure cycle;
(f) providing an analytic model for calculating a predicted resin viscosity of the part predicted to occur at a predetermined time during the curing process;
(g) calculating a predicted time-to-gel point for the part based on the predicted resin viscosity;
(h) measuring porosity of the part at the predetermined time during the curing process;
(i) predicting whether the porosity of the part will remain above a predetermined maximum acceptable level when the gel point is reached;
(j) increasing ambient pressure in the curing vessel by a predetermined increment when the porosity is predicted to remain above the predetermined maximum acceptable level when the gel point is reached;
(k) providing an analytic model for calculating a predicted number of compacted plies of the part predicted to occur at a predetermined time during the curing process;
(l) estimating an actual number of compacted plies of the part at the predetermined time during the curing process;
(m) comparing the predicted number of compacted plies to the actual number of compacted plies;
(n) adjusting the ambient pressure within the curing vessel by a predetermined increment when the actual number of compacted plies falls outside of a predetermined acceptable range;
(o) estimating an actual degree of cure of the part at a predetermined time during the curing process;
(p) comparing the actual degree of cure to a predetermined acceptable actual degree of cure;
(q) repeating steps a through p when the actual degree of cure falls below the acceptable actual degree of cure;
(r) providing, when the acceptable actual degree of cure has been achieved, an analytic model for determining when a predetermined acceptable theoretical degree of cure has been achieved;
and
(s) repeating steps o through r when the theoretical degree of cure is below the predetermined acceptable theoretical degree of cure.

17 more elements

A method for curing a composite material part in a curing vessel, comprising the steps of:

(a) obtaining initial property values for the composite material comprising the part wherein the part contains at least one ply;
(b) specifying an initial part temperature;
(c) determining an initial set of cure cycles;
(d) running a computer model simulation of each cure cycle in the initial set to predict the length of time which would be required for the cure cycle to satisfy a set of conditions wherein the set of conditions includes:
achieving a predetermined minimum acceptable degree of cure of the part;
compaction of all the plies of the part;
and
maintenance of the maximum internal part temperature below a predetermined maximum value during the curing process;
(e) selecting, as an initial cure cycle, the cure cycle in the initial set of cure cycles which satisfied the set of conditions in the shortest time;
(f) disposing the composite material part within the curing vessel for curing;
(g) setting initial curing vessel process conditions at the temperature and pressure levels dictated by the initial cure cycle;
(h) beginning the curing process;
(i) monitoring ambient levels of temperature and pressure within the curing vessel and adjusting the ambient levels as needed in accordance with the initial cure cycle;
(j) obtaining, at a predetermined time interval, real parameter values wherein the real parameters comprise:
maximum temperature of the part;
degree of cure of the part;
resin viscosity of the part;
porosity of the part;
and
the number of compacted plies of the part;
(k) comparing the real parameter values for temperature, degree of cure, resin viscosity, porosity and number of compacted plies to predicted parameter values for temperature, degree of cure, resin viscosity, porosity and number of compacted plies predicted by the computer simulations of the initial cure cycle;
(l) selecting a new cure cycle when at least one of the real parameter values falls outside of predetermined acceptable ranges of the predicted parameter values predicted by the initial cure cycle wherein the new cure cycle is selected by following steps c, d and e;
(m) adjusting the curing vessel process conditions in accordance with the conditions dictated by the new cure cycle when a new cycle is selected;
and
(n) continuing to monitor the curing process of the part by repeating steps i through m until the composite part has achieved the predetermined acceptable degree of cure wherein the cure process is ended.

22 more elements

Dependencies are inferred from the claim text.

Abstract

Claims18

Dependent claims

A method for controlling a curing process for curing a composite material part in a curing vessel, comprising the steps of:

placing the composite material part in the curing vessel;
selecting an initial cure cycle;
beginning the curing process of the composite material part in accordance with the initial cure cycle;
measuring an actual part temperature of the part during the curing process;
measuring a pressure within the curing vessel during the curing process;
directly measuring during the curing process at least one additional real part parameter value;
comparing the additional real part parameter value to a predicted part parameter value determined from a predictive analytic model;
selecting a new cure cycle periodically during the curing process when the additional real part parameter value falls outside of a predetermined acceptable range about the predicted part parameter value;
and
adjusting the curing process in accordance with the new cure cycle.

7 more elements

A method for controlling a curing process of a composite material part in a curing vessel, the part having at least one ply, the method comprising the steps of:

(a) providing an analytic model for calculating a predicted temperature of the part predicted to occur at a predetermined time during the curing process;
(b) measuring an actual maximum temperature of the part at the predetermined time during the curing process;
(c) comparing the predicted temperature to the actual maximum temperature;
(d) selecting a new cure cycle when the actual maximum temperature falls outside of an acceptable temperature range about the predicted temperature;
(e) adjusting an ambient temperature in the curing vessel in accordance with the new cure cycle;
(f) providing an analytic model for calculating a predicted resin viscosity of the part predicted to occur at a predetermined time during the curing process;
(g) calculating a predicted time-to-gel point for the part based on the predicted resin viscosity;
(h) measuring porosity of the part at the predetermined time during the curing process;
(i) predicting whether the porosity of the part will remain above a predetermined maximum acceptable level when the gel point is reached;
(j) increasing ambient pressure in the curing vessel by a predetermined increment when the porosity is predicted to remain above the predetermined maximum acceptable level when the gel point is reached;
(k) providing an analytic model for calculating a predicted number of compacted plies of the part predicted to occur at a predetermined time during the curing process;
(l) estimating an actual number of compacted plies of the part at the predetermined time during the curing process;
(m) comparing the predicted number of compacted plies to the actual number of compacted plies;
(n) adjusting the ambient pressure within the curing vessel by a predetermined increment when the actual number of compacted plies falls outside of a predetermined acceptable range;
(o) estimating an actual degree of cure of the part at a predetermined time during the curing process;
(p) comparing the actual degree of cure to a predetermined acceptable actual degree of cure;
(q) repeating steps a through p when the actual degree of cure falls below the acceptable actual degree of cure;
(r) providing, when the acceptable actual degree of cure has been achieved, an analytic model for determining when a predetermined acceptable theoretical degree of cure has been achieved;
and
(s) repeating steps o through r when the theoretical degree of cure is below the predetermined acceptable theoretical degree of cure.

17 more elements

A method for curing a composite material part in a curing vessel, comprising the steps of:

(a) obtaining initial property values for the composite material comprising the part wherein the part contains at least one ply;
(b) specifying an initial part temperature;
(c) determining an initial set of cure cycles;
(d) running a computer model simulation of each cure cycle in the initial set to predict the length of time which would be required for the cure cycle to satisfy a set of conditions wherein the set of conditions includes:
achieving a predetermined minimum acceptable degree of cure of the part;
compaction of all the plies of the part;
and
maintenance of the maximum internal part temperature below a predetermined maximum value during the curing process;
(e) selecting, as an initial cure cycle, the cure cycle in the initial set of cure cycles which satisfied the set of conditions in the shortest time;
(f) disposing the composite material part within the curing vessel for curing;
(g) setting initial curing vessel process conditions at the temperature and pressure levels dictated by the initial cure cycle;
(h) beginning the curing process;
(i) monitoring ambient levels of temperature and pressure within the curing vessel and adjusting the ambient levels as needed in accordance with the initial cure cycle;
(j) obtaining, at a predetermined time interval, real parameter values wherein the real parameters comprise:
maximum temperature of the part;
degree of cure of the part;
resin viscosity of the part;
porosity of the part;
and
the number of compacted plies of the part;
(k) comparing the real parameter values for temperature, degree of cure, resin viscosity, porosity and number of compacted plies to predicted parameter values for temperature, degree of cure, resin viscosity, porosity and number of compacted plies predicted by the computer simulations of the initial cure cycle;
(l) selecting a new cure cycle when at least one of the real parameter values falls outside of predetermined acceptable ranges of the predicted parameter values predicted by the initial cure cycle wherein the new cure cycle is selected by following steps c, d and e;
(m) adjusting the curing vessel process conditions in accordance with the conditions dictated by the new cure cycle when a new cycle is selected;
and
(n) continuing to monitor the curing process of the part by repeating steps i through m until the composite part has achieved the predetermined acceptable degree of cure wherein the cure process is ended.

22 more elements

Dependencies are inferred from the claim text.

Computer-controlled method for composite curing

Life of this patent

Abstract

Claims18