Wrought gamma titanium aluminide alloys modified by chromium, boron, and nionium
AssigneeGeneral Electric Company
InventorShyh-Chin Huang
Life of this patent
Estimating the term…
Abstract
A TiAl composition is prepared to have high strength and to have improved ductility by altering the atomic ratio of the titanium and aluminum to have what has been found to be an effective aluminum concentration and by addition of chromium, boron, and niobium according to the approximate formula Ti-Al.sub.46-48 Cr.sub.2 Nb.sub.2 B.sub.0.1-0.2. The composition is preferably prepared by casting, homogenization at a high temperature, and forging the homogenized casting.
Claims5
A cast and wrought body of alloy, said alloy consisting essentially of a gamma titanium aluminide modified by chromium, niobium, and boron according to the expression:
- Ti-Al.sub.46-50 Cr.sub.1-3 Nb.sub.1-5 B.sub.0.05-0.3.,
- said body having been homogenized for one to three hours at a temperature close to or above the alpha transus temperature, and
- said body having been wrought to cause a deformation thereof of at least 10% and annealed.
A cast and wrought body of alloy, said alloy consisting essentially of a gamma titanium aluminide modified by chromium, niobium, and boron according to the expression:
- Ti-Al.sub.46-50 Cr.sub.1-3 Nb.sub.2 B.sub.0.1-0.2.,
- said body having been homogenized for one to three hours at a temperature close to or above the alpha transus temperature, and
- said body having been wrought to cause a deformation thereof of at least 10% and annealed.
A cast and wrought body of alloy, said alloy consisting essentially of a gamma titanium aluminide modified by chromium, niobium, and boron according to the expression:
- Ti-Al.sub.46-50 Cr.sub.2 Nb.sub.1-5 B.sub.0.05-0.3.,
- said body having been homogenized for one to three hours at a temperature close to or above the alpha transus temperature, and
- said body having been wrought to cause a deformation thereof of at least 10% and annealed.
A cast and wrought body of alloy, said alloy consisting essentially of a gamma titanium aluminide modified by chromium, niobium, and boron according to the expression:
- Ti-Al.sub.46-48 Cr.sub.2 Nb.sub.2 B.sub.0.2.,
- said body having been homogenized for one to three hours at a temperature close to or above the alpha transus temperature, and
- said body having been wrought to cause a deformation thereof of at least 10% and annealed.
A cast and wrought body of alloy, said alloy consisting essentially of a gamma titanium aluminide modified by chromium, niobium, and boron according to the expression:
- Ti-Al.sub.46-48 Cr.sub.2 Nb.sub.2 B.sub.0.2.,
- said body having been homogenized for one to three hours at a temperature close to or above the alpha transus temperature, and
- said body having been wrought to cause a deformation thereof of at least 10% and annealed.
Dependencies are inferred from the claim text.