Focal track structures for X-ray anodes and method of preparation thereof
AssigneeGeneral Electric Company
InventorsDavid W. Woodruff, Minyoung Lee
Life of this patent
Estimating the term…
Abstract
An improved high performance x-ray tube having a rotating graphite anode therein and method of preparation thereof. The surface of a graphite anode body is oxidized in air for removing the surface damage caused during the machining of the anode body. The anode body is provided with a diffusion barrier layer of rhenium contiguously disposed on the substantially damage free surface of the anode body. An anode target layer is then deposited on top of the barrier layer.
Claims8
An x-ray tube anode comprising a graphite anode body wherein any damaged surface graphite has been removed by heating in air at about 650.degree.-900.degree. C. for about 45-90 minutes, and a focal track layer disposed on the surface of said graphite body for impingement by electrons to produce x-rays.
A method of improving adherence of a focal track layer of an anode of an x-ray tube to a graphite anode body of said tube comprising:
- shape forming a graphite substrate into said anode body having a surface with a focal track region thereon;
- oxidizing a layer on said surface damaged during said shape forming step by heating in air at about 650.degree.-900.degree. C. for about 45-90 minutes to expose an undamaged surface underneath said damaged layer;
- and
- depositing said focal track layer on top of said undamaged surface of said focal track region.
An improved x-ray tube comprising:
- a substantially evacuated and sealed envelope;
- a cathode structure positioned at a first end within said envelope, said cathode structure comprising a support, an electron emissive filament and a focussing cup mounted on said support, a pair of filament conductors for supplying heating current to said filament and a ground conductor to electrically ground said structure;
- an anode comprising a graphite anode body whereon any surface damage caused during shape forming has been removed by heating in air at about 650.degree.-900.degree. C. for about 45-90 minutes;
- a focal track layer contiguously disposed on top of said body for impingement by electrons emitted by said filament for producing x-ray;
- and rotating means positioned at a second end within said envelope for rotating said anode.
A method of producing a graphite substrate comprising:
- shape forming said substrate;
- and
- oxidizing any damaged graphite on said shape formed surface by heating in air at about 650.degree.-900.degree. C. for about 45-90 minutes to expose an undamaged surface underneath said damaged graphite.
A method of producing an improved anode for an x-ray tube comprising:
- shape forming a graphite substrate into an anode body having a surface with a focal track region thereon;
- oxidizing a layer on said surface damaged during said shape forming step by heating in air at about 650.degree.-900.degree. C. for about 45-90 minutes to expose an undamaged surface underneath said damaged layer;
- chemical vapor depositing a rhenium diffusion barrier layer on top of said undamaged surface of said region;
- and
- chemical vapor depositing an anode target layer of tungsten or tungsten-rhenium alloy on top of said diffusion barrier layer.
Dependencies are inferred from the claim text.