Method of producing low iron loss grain oriented silicon steel thin sheets having excellent surface properties
AssigneeKawasaki Steel Corporation
InventorsYukio Inokuti, Yoh Ito
Life of this patent
Estimating the term…
Abstract
It is a technical subject to advantageously avoid the degradation of surface properties in a low iron loss grain oriented silicon steel sheet as a material for transformers, particularly if it is intended to thin the gauge to 0.1.about.0.25 mm. A low iron loss grain oriented silicon steel thin sheet can stably be produced without causing the degradation of performances through strain relief annealing by considering a chemical composition in steel, optimizing the rolling conditions, particularly cold rolling conditions, and further forming heterogeneous microareas onto the steel sheet surface.
Claims9
A method of producing from a steel slab a low iron loss grain oriented silicon steel thin sheet having recrystallized grains in a (110)<001>
- orientation and having excellent surface properties, which comprises incorporating into the steel slab molybdenum, silicon and aluminum as an inhibitor, wherein the amounts of molybdenum, silicon and aluminum are
- Si:
- 3.1.about.4.5 wt %,
- Mo:
- 0.003.about.0.1 wt %,
- acid soluble Al:
- 0.005.about.0.06 wt %, and
- at least one of S and Se is present in an amount of 0.005.about.0.1 wt % in total;
- subjecting said steel slab to hot rolling in the presence of said molybdenum and preventing oxidation of the grain boundary to form a hot rolled steel sheet;
- subjecting the hot rolled steel sheet to primary cold rolling at a reduction of 10.about.60% and an intermediate annealing and a secondary cold rolling at a reduction of 75.about.90% to obtain a cold rolled thin sheet having a final gauge of 0.1.about.0.25 mm;
- subjecting the cold rolled thin sheet to decarburization and primary recrystallization annealing in a wet hydrogen atmosphere;
- and subjecting the thin sheet to high-temperature finish annealing.
A method of producing from a steel slab a low iron loss, high magnetic flux density grain oriented silicon steel thin sheet having recrystallized grains in a (110)<001>
- orientation and having excellent surface properties, which comprises incorporating into the steel slab molybdenum, silicon and aluminum as an inhibitor, wherein the amounts of molybdenum, silicon and aluminum are
- Si:
- 3.1.about.4.5 wt %,
- Mo:
- 0.003.about.0.1 wt %,
- acid soluble Al:
- 0.005.about.0.06 wt %, and
- at least one of S and Se is present in an amount of 0.005.about.0.1 wt % in total;
- subjecting said steel slab to hot rolling in the presence of said molybdenum and preventing oxidation of the grain boundary to form a hot rolled steel sheet;
- subjecting the hot rolled steel sheet to primary cold rolling at a
- reduction of 10.about.60% and an intermediate annealing and a secondary cold rolling at a reduction of 75.about.90% to obtain a cold rolled thin sheet having a final gauge of 0.1.about.0.25 mm;
- subjecting the cold rolled thin sheet to decarburization and primary recrystallization annealing in a wet hydrogen atmosphere;
- before or after said decarburization and primary recrystallization annealing step subjecting the cold rolled thin sheet to a treatment for the formation of surface modified heterogeneous microareas onto the surface of the thin sheet;
- and subjecting the thin sheet to high-temperature finish annealing.
In a method of producing a low iron loss grain oriented silicon steel thin sheet having recrystallized grains in a (110)<001>
- orientation, wherein a steel slab is subjected to hot rolling to form a hot rolled steel sheet, the step which comprises incorporating into the steel slab molybdenum, silicon and aluminum, the content of silicon being in the range of 3.1.about.4.5 wt %, the amount of acid soluble aluminum being in the range of 0.005.about.0.06 wt %, said slab also containing at least one of sulfur and selenium in an amount of 0.005.about.0.1 wt %, the step which comprises incorporating into the steel slab molybdenum in an amount of 0.003.about.0.1 wt %, and conducting said hot rolling in the presence of said molybdenum thereby preventing oxidation of the grain boundary in the formation of the hot rolled steel sheet.
Dependencies are inferred from the claim text.