High yield manufacturing process for silicon carbide
AssigneeThe Dow Chemical Company
InventorsAlan W. Weimer, Raymond P. Roach, John P. Henley
Life of this patent
Estimating the term…
Abstract
A process for preparing silicon carbide by carbothermal reduction which includes transporting, in a gaseous medium, a particulate reactive mixture of a silica source and a carbon source through a reaction zone. The heating rate of the atmosphere within the reaction zone is such that substantially all of the reactive mixture is heated at a heating rate of at least about 100.degree. C./second until an elevated temperature of at least 1800.degree. C. is reached. Either (1) carbon monoxide is added to the reaction zone or (2) a carbon monoxide level in the reaction is achieved in order to provide at least about 30 mole percent of the gases exiting the reaction zone to achieve a higher yield of silicon carbide.
Claims26
A process for preparing silicon carbide by carbothermal reduction, comprising transporting, in a gaseous medium, a particulate reactive mixture of a silica source and a carbon source through a reaction zone while adding carbon monoxide gas to the reaction zone at a rate such that carbon monoxide gas constitutes at least about 30 mole % of the gases exiting the reaction zone, the heating rate of the atmosphere within the reaction zone being such that substantially all of the reactive mixture is heated at a heating rate of at least about 100.degree. C./second until an elevated temperature of at least 1800.degree. C. is reached.
A process for preparing silicon carbide crystals by carbothermal reduction, comprising:
- (a) transporting a particulate reactive mixture of a silica source and a carbon source in a gaseous medium into a reactor, said reactor having
- (1) a reactant transport member, the reactant transport member having a walled chamber defining a hollow conduit, a cooling means for cooling the reactant transport member, and a gas flow space defined by an inner wall having an inner annular space, the inner annular space having an inlet and an exit at the distal end to allow gas to flow therethrough;
- (2) a reactor chamber, the reactor chamber having a wall defining a reaction zone, the chamber being in fluid communication with the reactant transport member;
- (3) a heating means, the heating means being suitable for heating the particulate reactive mixture in the reaction zone;
- and
- (4) a cooling chamber for cooling the reaction product, and transporting gases and resultant by-products, the cooling chamber having a wall defining a cooling zone and a cooling means, the cooling chamber being in fluid communication with the reactor chamber;
- the temperatures of the reactant transport member, reactor chamber, and cooling chamber being independently controllable such that the particulate reactive mixture can be fed continuously through the reactant transport member into the reaction zone and then into the cooling zone;
- (b) adding carbon monoxide gas to the reaction zone at a rate such that carbon monoxide gas constitutes at least about 30 mole % of the gases exiting the reaction zone while heating the particulate reactive mixture in the reaction zone at a heating rate of at least about 100.degree. C./second until an elevated temperature of at least 1800.degree. C. is reached to form a product;
- and
- (c) cooling the product in the cooling zone.
A process for preparing silicon carbide by carbothermal reduction, comprising transporting, in a gaseous medium, a particulate reactive mixture of a silica source and a carbon source through a reaction zone in which carbon monoxide constitutes at least about 30 mole percent of the gases exiting the reaction zone, the heating rate of the atmosphere within the reaction zone being such that substantially all of the reactive mixture is heated at a rate of at least about 100.degree. C./second until an elevated temperature of at least 1800.degree. C. is reached.
A process for preparing silicon carbide crystals by carbothermal reduction, comprising:
- (a) transporting a particulate reactive mixture of a silica source and a carbon source in a gaseous medium into a reactor, said reactor having
- (1) a reactant transport member, the reactant transport member having a walled chamber defining a hollow conduit, a cooling means for cooling the transport member, and a gas flow space defined by an inner wall having an inner annular space, the inner annular space having an inlet at a proximal end and an exit at the distal end to allow gas to be flowed therethrough;
- (2) a reactor chamber, the reactor chamber having a wall defining a reaction zone, the reaction zone having a carbon monoxide level which constitutes at least about 30 mole percent of the gases exiting the reaction zone, the chamber being in fluid communication with the reactant transport member;
- (3) a heating means, the heating means being suitable for heating the particulate reactive mixture in the reaction zone;
- and
- (4) a cooling chamber, for cooling the reaction product, transporting gases and resultant by-product, the cooling chamber having a wall defining a chamber being in fluid communication with the reactor chamber,
- the temperature of the reactant transport member, reactor chamber, and cooling chamber being independently controllable such that the particulate reactive mixture can be fed continuously through the reactant transport member into the reaction zone and then into the cooling zone;
- (b) heating the particulate reactive mixture in the reaction zone at a heating rate of at least about 100.degree. C./second until an elevated temperature of at least 1800.degree. C. is reached to form a product;
- and
- (c) cooling the product in the cooling zone.