Method of forming a trailing edge on a steam turbine blade and the blade made thereby
AssigneeWestinghouse Electric Corp.
InventorDennis R. Amos
Life of this patent
Estimating the term…
Abstract
A steam turbine blade is provided having a trailing edge portion formed from an erosion resistant material deposited on the blade airfoil by a friction surfacing method. According to the method, a rotating consumable rod of erosion resistant material is placed in contact under axial load against a bonding surface formed on the airfoil, thereby causing a portion of the rod adjacent the bonding surface to be plasticized. The rod then traverses the surface linearly leaving in its wake a layer of erosion resistant material bonded to the airfoil by a high quality metallurgical bond. The layer is then ground to form the smooth contour desired for the trailing edge.
Claims17
A method of making a steam turbine blade having (i) an airfoil partially formed from a first material and (ii) an erosion resistant trailing edge, comprising the step of forming said erosion resistant trailing edge on said airfoil by the steps of:
- (a) forming a bonding surface on said airfoil adapted to receive said erosion resistant trailing edge;
- (b) rotating a rod formed from a second material;
- (c) placing said rotating rod in contact with said airfoil bonding surface;
- (d) pressing said rotating rod against said bonding surface with an axial force, thereby plasticizing a portion of said rod adjacent said bonding surface, said pressing of said rod initially performed while simultaneously moving said rod approximately linearly relative to said bonding surface so that contact between said rod and said bonding surface is made with a running start;
- and
- (e) moving said rotating rod approximately linearly along said bonding surface at a predetermined speed while maintaining said axial force, thereby consuming said rod and bonding said plasticized portion of said rod to said bonding surface, whereby an erosion resistant trailing edge is formed on said airfoil.
A method of making a steam turbine blade airfoil having a first portion formed from a first material and a second portion formed from a second material, comprising the step of forming a layer of said second material on said first portion of bonding said second material to said first portion by the steps of:
- (a) forming said second material into a consumable rod;
- (b) rotating said rod;
- and
- (c) initially pressing said rotating rod axially against said airfoil while simultaneously moving said rod along said airfoil in a direction approximately perpendicular to the axis of rotation of said rod.
A steam turbine blade having a root portion and an airfoil portion extending from said root portion, said airfoil portion having an edge portion and a center portion disposed adjacent said edge portion, said center portion formed from a first material, at least a first portion of said edge portion formed from a second material and bonded to said center portion, said blade made by a process comprising the steps of:
- (a) placing a rotating rod formed from said first material in contact with said center portion;
- (b) pressing said rotating rod against said center portion with an axial force, thereby plasticizing a portion of said rod adjacent said center portion, said rotating rod initially pressed against said center portion while simultaneously moving said rod approximately linearly relative to said center portion so that contact between said rod and said center portion is made with a running start;
- and
- (c) moving said rotating rod approximately linearly along said center portion while maintaining said axial force, thereby consuming said rod and bonding said plasticized portion of said rod to said center portion, whereby said first portion of said edge portion is formed on said center portion.
Dependencies are inferred from the claim text.