Abstract
The invention provides a novel metallic composition and method of using the same. More particularly, the invention affords a tool steel and a method of heat treating the tool steel. In one of the preferred embodiments the tool steel includes about 0.50 to about 0.65 percent by weight carbon, about 0.090 to about 1.45 percent by weight manganese, up to about 0.030 percent by weight phosphorus, about 0.035 to about 0.070 percent by weight sulfur, about 1.10 to about 1.90 percent by weight chromium, about 0.15 to about 0.40 percent by weight nickel and about 0.20 to about 0.40 percent by weight copper. In one of the preferred embodiments of the present invention the tool steel is heat treated utilizing a heat treatment schedule that includes the steps of a preheat, austenization and a double temper.
Claims19
A metallic composition comprising at least about 92 percent by weight iron (Fe), from about 0.50 to about 5.65 percent by weight carbon (C), from about 0.090 to about 1.45 percent by weight manganese (Mn), up to about 0.030 percent by weight phosphorus (P), from about 0.030 to about 0.080 percent by weight sulfur (S), from about 1.30 to about 1.70 percent by weight chromium (Cr), from about 0.050 to about 0.80 percent by weight silicon (Si), at least about 0.20 percent by weight copper (Cu), from about 0.15 to about 0.40 percent by weight nickel (Ni) up to about 0.010 percent by weight vanadium (V), up to about 0.20 percent by weight molybdenum (Mo), less than about 0.05 percent by weight cobalt (Co), less than about 0.03 percent by weight tungsten (W), less than about 0.001 percent by weight titanium (Ti) and less than about 0.20 percent by weight aluminum (Al).
A method of producing a tool or die comprising the steps of:
- (A) providing a section of metal comprising at least about 92 percent by weight iron (Fe), up to about 0.95 percent by weight carbon (C), about 0.075 to about 1.6 percent by weight manganese (Mn), about 0.020 to about 0.090 percent by weight sulfur (S), about 1 to about 2 percent by weight chromium (Cr) and about 0.10 to about 0.50 percent by weight nickel (Ni);
- (B) austenitizing such metal;
- and
- (C) tempering such metal;
- wherein during said austenitizing step (B) such metal is initially heated to an equalization temperature of from about 1,625.degree. F. to about 1,675.degree. F. for a period of from about one to about three hours for about every inch of cross section measured at the thickest portion of such metal, then such metal is heated to a temperature of from about 1,475.degree. F. to about 1,525.degree. F. for from about thirty to about ninety minutes for about every inch of cross section measured at the thickest portion of such metal and then such metal is oil quenched.
A method of producing a tool or die consisting of the steps of:
- (A) providing a section of metal having a weight in excess of about 120 pounds and comprising at least about 92 percent by weight iron (Fe), from about 0.050 to about 0.65 percent by weight carbon (C), from about 0.090 to about 1.45 percent by weight manganese (Mn), up to about 0.030 percent by weight phosphorus (P), from about 0.030 to about 0.080 percent by weight sulfur (S), from about 1.30 to about 1.70 percent by weight chromium (Cr), from about 0.50 to about 0.80 percent by weight silicon (Si), at least about 0.20 percent by weight copper (Cu), from about 0.15 to about 0.40 percent by weight nickel (Ni) up to about 0.010 percent by weight vanadium (V), up to about 0.20 percent by weight molybdenum (Mo), less than about 0.05 percent by weight cobalt (Co), less than about 0.03 percent by weight tungsten (W), less than about 0.001 percent by weight titanium (Ti) and less than about 0.20 percent by weight aluminum (Al);
- (B) normalizing such section of metal at an equalization temperature of from about 1,575.degree. F. to about 1,675.degree. F. for about every inch of cross section measured at the heaviest portion of such metal;
- and
- (C) air cooling such section of metal to room temperature.
Dependencies are inferred from the claim text.