US 5,180,775 AGranted
Blends of copoly(arylene sulfide) and ethylene-propylene rubber
AssigneeEastman Kodak Company
InventorsShriram Bagrodia, David R. Fagerburg, Steven Gedon, Joseph J. Watkins, Paul B. Lawrence, Mark Rule
Life of this patent
Estimating the term…
Abstract
Disclosed is a composition comprising (A) from 99.9 to 60 weight percent, based on the weight of the composition, of a copoly(arylene sulfide) and (B) from 0.1 to 40 weight percent, based on the weight of the composition, of an ethylene-propylene rubber.
Claims4
A composition comprising
- (A) from 99.9 to 90 weight percent, based on the weight of the composition, of a copoly(arylene sulfide) corresponding to the structure
- [(--A--S--).sub.1-x (--A--S--S--).sub.x ].sub.n
- wherein A is a divalent substituted or unsubstituted aromatic radical, x is in the range of 0.5 to 0.001 and n is at least 25, and
- (B) from 0.1 to 10 weight percent, based on the weight of the composition, of a maleated ethylene-propylene rubber having an amount of ethylene in the range of 40 to 90 mole percent and an amount of propylene in the range of 60 to 10 mole percent, based on the total moles of ethylene and propylene.
1 more element
A composition comprising
- (A) from 99 to 90 weight percent, based on the weight of the composition, of a copoly(phenylene sulfide) corresponding to the structure
- [(--A--S--).sub.1-x (--A--S--S--).sub.x ].sub.n
- wherein A is a divalent phenylene radical, x is in the range of 0.5 to 0.001 and n is at least 50, and
- (B) from 1 to 10 weight percent, based on the weight of the composition, of a maleated ethylene-propylene rubber having an amount of ethylene in the range of 50 to 75 mole percent and an amount of propylene in the range of 50 to 25 mole percent, based on the total moles of ethylene and propylene.
1 more element