Modified rosin esters and their use in printing inks
AssigneeWestvaco Corporation
InventorJoseph W. LeVine
Life of this patent
Estimating the term…
Abstract
A binder for use in gravure printing ink formulations comprising a modified rosin ester resinate prepared by forming a rosin-dienophile adduct, reacting the adduct with a polyfunctional hydroxy compound to form an ester and reacting with an acrylic-containing polymer to form a hard rosin ester. The polymer-modified rosin ester resinate is formed by reacting the prepared hard rosin ester with a rosin-dienophile adduct and an acrylic-containing polymer, reacting the product thereof with reactive zinc, followed by a reaction with lime, dehydrating the resinate product by refluxing, and adjusting its viscosity with a hydrocarbon solvent.
Claims3
A method of making a polymer-modified rosin ester resinate comprising the steps of:
- (a) reacting molten rosin selected from the group consisting of tall oil rosin, wood rosin, and gum rosin with a sufficient amount of dienophile selected from the group consisting of fumaric acid, maleic acid, maleic anhydride, acrylic acid, methacrylic acid, citraconic acid, and itaconic acid to form a rosin adduct;
- (b) blending the rosin adduct of step (a) with a polymer-modified rosin ester prepared by the steps of esterifying an additional amount of the rosin adduct with a polyfunctional hydroxy compound to form an esterified rosin resin, and reacting said esterified rosin resin with an acrylic containing polymer selected from the group consisting of mixtures of a polymer of acrylic acid, organic ester derivatives of acrylic acid, methacrylic acid, organic ester derivatives of methacrylic acid, mixtures thereof, and a member selected from the group consisting of styrene, alpha methyl styrene, ethylene vinyl acetate, and a combination thereof;
- (c) reacting the blend of step (b) with a member selected from the group consisting of reactive zinc, MgO, lime, and mixtures thereof, in the form of a slurry;
- (d) heating the reaction product of step (c) at reflux until the resinate is dehydrated;
- and
- (e) adjusting the viscosity of the resinate with hydrocarbon solvent.
Dependencies are inferred from the claim text.