US 5,180,482 AGranted

Thermal annealing of palladium alloys

AssigneeAT&T Bell Laboratories

InventorsJoseph A. Abys, Igor V. Kadija, Joseph J. Maisano, Jr., Shohei Nakahara

Life of this patent

Estimating the term…

Loading patent…

Abstract

This invention is concerned with production of electrical devices comprising an electrodeposited conductive region free from cracking defects. In the production of a contact portion of the device from a metal strip electroplated with a conductive stripe of an alloy, the stripe exhibited, upon stamping and forming operation, cracked areas. Typically, the stripe coating on the metal strip, such as a copper bronze material, includes a layer of nickel, a layer of palladium alloyed with nickel, cobalt, arsenic or silver, and a flash coating of hard gold. The cracking defects were eliminated by subjecting the plated strip to an annealing treatment prior to the stamping and forming operation. After the heat-treatment, the stripe was free from cracks and separations between the successive layers.

Claims8

Dependent claims

The process of fabricating an electrical device having at least one contact comprising a conductive region, which comprises,

electroplating on at least a portion of a metal base a plated deposit layer comprising from 20 to 80 mole percent palladium remainder nickel, subjecting at least the plated portion to an annealing process, permitting the annealed sample to cool to room temperature, and forming the plated metal base into a desired form, said annealing and cooling steps being conducted in an inert atmosphere, wherein,
prior to said forming step, at least the plated portion is subjected to an annealing process,
said annealing is a Rapid Thermal Anneal (RTA) heat treatment which comprises raising the plated portion from the plating temperature to a temperature within a range from 575.degree. to 800.degree. C. within a period of time ranging from 1 second to 30 seconds and maintaining the plated portion at said holding temperature for a period of from 1 to 30 seconds, the total time of heat-treatment being sufficient to anneal the plated deposit so as to eliminate cracking of the deposit as the result of the forming step but insufficient to result in the loss of spring in the metal base.

Dependencies are inferred from the claim text.