Method for making lithoplate having improved grainability
AssigneeAluminum Company of America
InventorsStephen C. Byrne, John K. McBride, James R. Weaver
Life of this patent
Estimating the term…
Abstract
An improved method of treating an ingot to be made into lithoplate. The method also includes (a) providing a non-heat treatable aluminum alloy containing magnesium; (b) homogenizing said alloy; (c) rolling said alloy to form a sheet or plate; (d) heating said sheet or plate for a temperature and time sufficient to permit magnesium to migrate to the surface of said metal; and (e) cold rolling said sheet or plate stock to a finished gauge workpiece.
Claims12
A method for producing an aluminum lithoplate comprising:
- (a) providing a non-heat treatable aluminum alloy containing at least 0.1 weight percent magnesium;
- (b) heating said alloy to a temperature of 1075.degree.-1200.degree. F. for at least 4 hours;
- (c) rolling said alloy to form a sheet or plate;
- (d) heating said sheet or plate above approximately 700.degree. F. for at least 1 hour;
- and
- (e) cold rolling said sheet or plate stock to a finished gauge workpiece.
In The production of lithoplate sheet or plate wherein at least one side of an aluminum alloy sheet is chemically or electrochemically grained, the improvement wherein said sheet or plate is produced by:
- heating a sheet of a non-heat treatable aluminum alloy containing at least 0.1 weight percent magnesium above a temperature of 700.degree. F. and maintaining said temperature for at least one hour to cause the migration of said magnesium towards the interface between the surface of the metal and the native oxide layer.
A method for producing a crystalline grain structure beneath the surface of the oxide layer of an aluminum lithoplate alloy comprising the steps of:
- (a) providing a non-heat treatable aluminum lithoplate alloy containing magnesium and rolling it a predetermined gauge;
- and
- (b) heating said alloy for above approximately 700.degree. F. for at least 1 hour.
A method for treating aluminum to provide a roughened surface thereon suitable for lithographic uses, said method comprising the steps of:
- forming an ingot of a non-heat treatable aluminum alloy containing at least 0.1 weight percent magnesium;
- homogenizing said ingot for a period of time suitable to insure homogenization of the ingot;
- rolling said ingot to form reroll stock;
- heating said reroll stock above approximately 700.degree. F. for at least 2 hours to cause migration of said magnesium towards the surface of said ingot;
- cold rolling the reroll stock to a finished gauge workpiece;
- and
- providing means for graining at least one surface of the workpiece.
A method for producing an aluminum lithoplate comprising:
- (a) providing a non-heat treatable aluminum alloy containing at least 0.1 weight percent magnesium;
- (b) heating said alloy to a temperature of 1075.degree.-1200 .degree. F. for at least 4 hours;
- (c) rolling said alloy to form a sheet or plate;
- (d) heating said sheet or plate above approximately 700.degree. F. for at least 1 hour;
- and
- (e) cold rolling said sheet or plate stock.