Dental porcelain for titanium and titanium alloys
AssigneeAmerican Thermocraft Corporation
InventorsCarlino Panzera, Arun Prasad
Life of this patent
Estimating the term…
Abstract
Porcelain compositions suitable for use as porcelain layers on metal base dental restorations have fusion temperatures of about 800.degree. C. and lower. The compositions may be employed as coatings on titanium and titanium alloy bases since the compositions have thermal expansion values close to those of titanium and its alloys. A method is also provided for forming dental restorations with relatively inexpensive and biocompatible metal bases and low fusing dental porcelains.
Claims16
A biocompatible porcelain composition consisting essentially of:
- Component (A) 50-70 percent by weight silicon dioxide,
- Component (B) 7-33 percent by weight boron oxide,
- Component (C) at least 8 percent by weight zinc oxide,
- Component (D) up to 4 percent by weight aluminum oxide,
- Component (E) up to 4 percent by weight titanium dioxide,
- Component (F) up to 12 percent by weight sodium oxide,
- Component (G) up to 8 percent by weight potassium oxide,
- Component (H) up to 3 percent by weight cerium oxide,
- Component (I) up to 1 percent by weight zirconium oxide, and
- Component (J) up to 1 percent by weight of a complex of
- yttrium oxide and cerium oxide, said composition having a thermal expansion coefficient close to that of titanium and a fusion temperature of less than about 800.degree. C.
A biocompatible porcelain composition consisting essentially of a mixture of a first component mixture and a second component mixture, said first component mixture comprising 70-80 percent by weight of said porcelain composition and consisting essentially of:
- Component (A) 50-70 percent by weight silicon dioxide,
- Component (B) 7-33 percent by weight boron oxide,
- Component (C) at least 8 percent by weight zinc oxide,
- Component (D) up to 4 percent by weight aluminum oxide,
- Component (E) up to 4 percent by weight titanium dioxide,
- Component (F) up to 12 percent by weight sodium oxide,
- Component (G) up to 8 percent by weight potassium oxide,
- Component (H) up to 3 percent by weight cerium oxide,
- Component (I) up to 1 percent by weight zirconium oxide, and
- Component (J) up to 1 percent by weight of a complex of
- yttrium oxide and cerium oxide,
- said second component mixture comprising 20-30 percent by weight of said porcelain composition and consisting essentially of:
- Component (K) up to 100 percent by weight titanium dioxide,
- Component (L) up to 100 percent by weight cerium oxide,
- Component (M) up to 100 percent by weight stannous oxide, and
- Component (N) up to 100 percent by weight zinc oxide,
- said porcelain composition having a thermal expansion coefficient close to that of titanium and a fusion temperature of about 800.degree. C. or lower.
A porcelain composition as defined in claim 18, wherein said first component mixture consists essentially of Components (A), (B), (C), and (E).
A biocompatible porcelain composition consisting essentially of 50-70 weight percent silicon dioxide, 7-33 weight percent boron oxide, at least 8 weight percent zinc oxide and up to 4 weight percent aluminum oxide, said porcelain composition having a thermal expansion coefficient close to that of titanium and a fusion temperature of less than about 800.degree. C.
Dependencies are inferred from the claim text.