Process for making para-aramid fibers having high tenacity and modulus by microwave annealing
AssigneeE. I. Du Pont de Nemours and Company
InventorsSibbley P. Gauntt, Hua-Feng Huang
Life of this patent
Estimating the term…
Abstract
A process is disclosed for heating never-dried para-aramid fibers containing 20 to 200 wt % water, based on dry polymer weight to form a fiber having a modulus of greater than 800 gpd while retaining a high tenacity. The fibers are heated in one or more microwave resonant cavity applicators to a temperature of 250.degree. C. to 425.degree. C. and preferably 270.degree. C. to 310.degree. C. while under a tension of 0.2 to 10 grams per denier. The preferred para-aramid is poly(p-phenylene terephthalamide). Fibers having a density of less than 1.43 g/cc can be made; and fibers having moduli greater than 1100 gpd can be made.
Claims14
A process comprising:
- a) feeding never-dried para-aramid fibers containing from 0.2 to 2.0 grams of water per gram of dry filament to at least one microwave resonant cavity applicator operated at frequencies of from 100 to 10000 MHz and
- b) thereby, heating the fibers, at a rate at least 1000.degree. C. per second, to a temperature of from 200.degree. C. to 550.degree. C. in 0.05 to 0.5 second while the para-aramide fibers are under a tension of at least 0.2 grams per denier
- to provide fibers having a modulus of at least 800 grams per denier.
A filament consisting essentially of poly(p-phenylene terephthalamide) and having a longitudinal axis and a diameter wherein the filament contains internal cracks substantially parallel with the longitudinal axis and each crack having a length generally at least ten times the diameter of the filament
- wherein the cracks, (i) do not breach the surface of the filament;
- and (ii) result in internal voids to yield filaments of a density of 1.36 to 1.43 g/cc.
Dependencies are inferred from the claim text.