Rubber surface identification coating and rubber products derived therefrom
AssigneeThe Goodyear Tire & Rubber Company
InventorsBharat K. Kansupada, Larry L. Mershon, Christopher J. Koscho
Life of this patent
Estimating the term…
Abstract
The marking of an uncured or partially cured rubber surface with a marking, or identifying coating, which basically, disappears upon curing the rubber. In one aspect, the coating is applied as a suspension or solution in a specified solvent mixture. An article can be produced thereby as a cured assembly of rubber components.
Claims7
A substantially white composition is provided which is comprised of (A) 100 parts by weight of fine particle sized zinc stearate, a melting point of less than 135.degree. C., and (B) as a binder therefor, about 10 to about 15 parts by weight of a non-reactive alkyl phenol formaldehyde resin characterized by having a melting point in a range of about 80.degree. C. to about 120.degree. C., (ASTM E28), and soluble in an organic solvent having a KB in a range of about 28 to about 38, and (C) about 0.05 to about 0.3 parts by weight carbon black and/or silica.
A method of marking an uncured rubber article which comprises coating at least one surface of an uncured rubber article with a coating composition and drying said coated surface;
- wherein said coating composition is substantially white and comprises (A) 100 parts by weight Zinc stearate, (B) as a binder therefor, about 10 to about 15 parts by weight of a non-reactive alkyl phenol formaldehyde resin characterized by having a melting point in a range of about 80.degree. C. to about 120.degree. C. and soluble in an organic solvent having a KB value in a range of about 28 to about 38, about 0.05 to about 0.3 parts by weight carbon black and/or silica, and (D) about 150 to about 300 parts by weight organic solvent, wherein said solvent has a KB value in the range of about 30 to about 38, and has an aromatic hydrocarbon content of less than about one weight percent.
A method of manufacturing rubber article comprises the steps of (A) providing a marked rubber composition containing a curative therefor and having an identifying substantially white colored marking coating composition thereof, (B) assembling at least one of said marked rubber composition components together to form an article of one or more rubber components, and (C) curing said article under conditions of an elevated pressure and a temperature of at least about 135.degree. C.;
- wherein said substantially white color of the marking composition visibly disappears;
- wherein said marking composition is comprised of (A) 100 parts by weight of zinc stearate, (B) as a binder therefor, about 10 to about 15 parts by weight of a non-reactive alkyl phenol formaldehyde resin characterized by having a melting point in range of about 90.degree. C. to about 110.degree. C. and soluble in an organic solvent having a KB in a range of about 28 to about 38, (C) about 0.05 to about 0.3 parts by weight carbon black and/or silica.