Heat-resisting aluminum alloy
AssigneeNissan Motor Co., Ltd.
InventorsMasahiko Shioda, Syunsuke Suzuki, Akira Matsuyama, Yoshihiro Maki
Life of this patent
Estimating the term…
Abstract
A heat-resisting aluminum alloy contains manganese ranging from 6 to 8% by weight, iron ranging from 0.5 to 2% by weight, zirconium ranging from 0.03 to 0.5% by weight, and copper ranging from 2 to 5% by weight, the balance being essentially aluminum. The aluminum alloy has been confirmed to be high in mechanical strength both at ordinary temperatures and at high temperatures while to be suitable for producing an article by using so-called atomization process.
Claims9
A method for producing a heat-resisting light alloy article, consisting essentially of the steps of:
- preparing a parent metal having a composition consisting essentially of manganese ranging from 6 to 8% by weight, greater than about 1% and less than or equal to about 2% by weight of iron, zirconium ranging from 0.03 to 0.5% by weight, copper ranging from 2 to 5% by weight, and the balance essentially aluminum;
- superheating 150.degree. C. over the melting point of said parent metal to obtain a superheated molten metal of said parent metal;
- spraying said superheated molten metal to obtain atomized powder particles;
- and
- forming said powder particles into a predetermined shape.
A heat-resisting aluminum alloy consisting essentially of manganese ranging from 6 to 8% by weight, iron ranging from 1.5 to 2.0% by weight, zirconium ranging from 0.03 to 0.5% by weight, copper ranging from 2 to 5% by weight, and the balance essentially aluminum.
A material suitable for making an article by employing an atomization process in which molten parent metal of the material is atomized to obtain powder particles, said material consisting essentially of manganese ranging from 6 to 8% by weight, iron ranging from 1.5 to 2.0% by weight, zirconium ranging from 0.03 to 0.5% by weight, copper ranging from 2 to 5% by weight, and the balance essentially aluminum.
A component part of an automotive engine made of a material consisting essentially of manganese ranging from 6 to 8% by weight, iron ranging from 1.5 to 2.0% by weight, zirconium ranging from 0.03 to 0.5% by weight, copper ranging from 2 to 5% by weight, and the balance essentially aluminum.
A method for producing a heat-resisting light alloy article, consisting essentially of:
- preparing a parent metal having a composition consisting essentially of manganese ranging from 6 to 8% by weight, an iron content of from 1.5 to 2.0% by weight, zirconium ranging from 0.03 to 0.5% by weight, copper ranging from 2 to 5% by weight, and the balance essentially aluminum;
- melting said parent metal to obtain a molten metal of said parent metal;
- spraying said molten metal to obtain atomized powder particles;
- and
- forming said powder particles into a predetermined shape.
Dependencies are inferred from the claim text.