Palladium alloys for dental implant restorations
AssigneeIvoclar N.A.
InventorsStephen P. Schaffer, Patrick J. McCabe, Bernt-Roger Gustafsson
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeIvoclar N.A.
InventorsStephen P. Schaffer, Patrick J. McCabe, Bernt-Roger Gustafsson
Estimating the term…
The present invention relates to alloys containing about 50-90% palladium, 0-37% gold, 0-3% platinum, 0-35% silver, 0.5-8% gallium, 0-8% tin, and up to 0.2% of a grain refiner selected from the group consisting of iridium, rhenium and ruthenium, or mixtures thereof. In order to withstand the forces of mastication over long spans or cantilever sections, the alloys are more rigid than conventional palladium based alloys. The alloys may be utilized for conventional crown and bridgework or may be fabricated into a number of different prostheses for use on dental implants. These applications include, for example, metal base plates for dentures, metal retaining bars for removable or fixed removable dentures, full metal coverage crowns and bridges, and metal substructures to be veneered with resin or porcelain materials.
A palladium-based alloy for use in dental implant restorations consisting essentially, by weight, of essentially about 50-61% palladium, 35-40% gold, 0.5-2.5% silver, 2-8% gallium, 0-8% indium, 0-8% tin, 0.01-0.1% rhenium, and 0.01-0.1% ruthenium.
A palladium-based alloy for use in dental implant restorations consisting essentially, by weight, of essentially about 50-61% palladium, 25-37% silver, 1.8-3% gold, 4-7% tin, 0.5-3% gallium, 0.5-3% indium, 0-2% platinum, 0.01-0.1% rhenium and 0.01-0.1% ruthenium.
A palladium-based alloy for use in dental implant restorations consisting, by weight, of about 77-95% palladium, 2-3% gold, 2-3% silver, 0-6% gallium, 0-6% indium, 0-6% tin, 0.01-0.1% rhenium, and 0.01-0.1% ruthenium.