Method of forming membranes useful for separation of gases

A membrane assembly comprising a porous ceramic support bearing a membrane surface layer of dried alumina of thickness of 8-200 microns prepared by the process which comprises

• loading the outer layers of macropore of a porous ceramic carrier with blocking liquid thereby forming a porous ceramic support layer bearing outer layers of macropores loaded with adsorbed blocking liquid;
• contacting said outer layers of macropores of said porous ceramic carrier layer loaded with adsorbed blocking liquid with an aluminum alkoxide sol;
• maintaining said outer layers of macropores of said porous carrier layer loaded with adsorbed blocking liquid in contact with said aluminum alkoxide sol for an adsorption period during which said alkoxide sol is adsorbed as a surface layer on the surface of said porous carrier layer;
• drying said porous support layer bearing (i) outer layers of macropores loaded with adsorbed blocking liquid and (ii) a surface layer of said alkoxide sol during a controlled drying period at 20.degree. C.-100.degree. C. during which said adsorbed blocking liquid migrates outwardly toward the surface of said porous ceramic carrier layer during drying and minimizes migration of said alkoxide sol into said porous ceramic carrier layer as drying continues thereby forming a dried porous ceramic carrier layer bearing a surface layer of dried alkoxide sol;
• calcining said porous ceramic carrier layer bearing said surface layer of dried alkoxide sol at a calcining temperature of 400.degree. C.-500.degree. C. thereby decomposing said alkoxide and forming a porous carrier layer bearing a surface layer of decomposed alkoxide sol;
• and
• recovering said porous ceramic carrier layer bearing a surface layer of decomposed alkoxide sol.

The method of preparing a membrane assembly containing (i) a porous ceramic carrier layer characterized by mechanical strength and (ii) a porous surface layer which comprises

• loading the outer layers of macropores of a porous ceramic carrier with blocking liquid thereby forming a porous ceramic support layer bearing outer layers of macropores loaded with adsorbed blocking liquid;
• contacting said outer layers of macropores of said porous ceramic carrier layer, with adsorbed blocking liquid with an aluminum alkoxide sol containing peptizing agent;
• maintaining said outer layers of macropores of said porous carrier layer loaded with adsorbed blocking liquid in contact with said aluminum alkoxide sol for an adsorption period during which said alkoxide sol is adsorbed as a surface layer on the surface of said porous carrier layer;
• drying said porous support layer bearing (i) outer layers of macropores loaded with adsorbed blocking liquid and (ii) a surface layer of said alkoxide sol during a controlled drying period during which said adsorbed blocking liquid migrates outwardly toward the surface of said porous ceramic carrier layer during drying and minimizes migration of said alkoxide sol into said porous ceramic carrier layer as drying continues thereby forming a dried porous ceramic carrier layer bearing a surface layer of dried alkoxide sol;
• calcining said porous ceramic carrier layer bearing said surface layer of dried alkoxide sol at a calcining temperature of 400.degree. C.-500.degree. C. thereby decomposing said alkoxide and forming a porous carrier layer bearing a surface layer of decomposed alkoxide sol;
• and
• recovering said porous ceramic carrier layer bearing a surface layer of decomposed alkoxide sol.

The method of preparing a membrane assembly containing (i) a porous ceramic carrier layer characterized by mechanical strength and (ii) a porous surface layer which comprises

• loading the outer layers of macropore of a porous ceramic carrier with ethanol blocking liquid thereby forming a porous ceramic support layer bearing outer layers of macropores loaded with adsorbed blocking liquid;
• contacting said outer layers of macropores of said porous ceramic carrier layer loaded with said ethanol adsorbed blocking liquid with an aluminum tri-isopropoxide sol;
• maintaining said outer layers of macropores of said porous carrier layer loaded with said ethanol adsorbed blocking liquid in contact with said aluminum tri-isopropoxide sol for an adsorption period during which said sol is adsorbed as a surface layer on the surface of said porous carrier layer;
• drying said porous support layer bearing (i) outer layers of macropores loaded with said ethanol adsorbed blocking liquid and (ii) a surface layer of said aluminum tri-isoproxide sol during a controlled drying period at 20.degree. C.-100.degree. C. during which said adsorbed ethanol blocking liquid migrates outwardly toward the surface of said porous ceramic carrier layer during drying and minimizes migration of said aluminum tri-isopropoxide sol into said porous ceramic carrier layer as drying continues thereby forming a dried porous ceramic carrier layer bearing a surface layer of dried aluminum tri-isopropoxide sol;
• calcining said porous ceramic carrier layer bearing said surface layer of dried aluminum tri-isopropoxide sol at a calcining temperature of 400.degree. C.-500.degree. C. thereby decomposing said aluminum tri-isopropoxide and forming a porous carrier layer bearing a surface layer of decomposed aluminum tri-isopropoxide sol;
• and
• recovering said porous ceramic carrier layer bearing a surface layer of decomposed aluminum tri-isopropoxide sol.