High temperature crystalline superconductors from crystallized glasses
AssigneeArch Development Corporation
InventorDonglu Shi
Life of this patent
Estimating the term…
Abstract
A method of preparing a high temperature superconductor from an amorphous phase. The method involves preparing a starting material of a composition of Bi.sub.2 Sr.sub.2 Ca.sub.3 Cu.sub.4 Ox or Bi.sub.2 Sr.sub.2 Ca.sub.4 Cu.sub.5 Ox, forming an amorphous phase of the composition and heat treating the amorphous phase for particular time and temperature ranges to achieve a single phase high temperature superconductor.
Claims7
A method of preparing a superconductor comprising a crystalline phase with a high critical temperature, comprising the steps of:
- preparing a starting material of a chemical or mechanical mixture having a composition selected from the group consisting of Bi.sub.2 Sr.sub.2 Ca.sub.3 Cu.sub.4 O.sub.x ;
- Bi.sub.2 Sr.sub.2 Ca.sub.4 Cu.sub.5 O.sub.x and mixtures thereof;
- forming an amorphous solid phase by melting said starting material to form a molten mixture and rapidly quenching said molten mixture;
- and
- heat treating said amorphous solid phase at a temperature of about 870.degree. C. for about 7-10 days and stopping said annealing, causing transformation from said amorphous phase to said crystalline phase composed substantially of a single phase superconductor exhibiting a T.sub.c of about 110.degree. K. as determined by the measurement of substantially zero resistivity for said superconductor.
A method of preparing a superconductor comprising substantially a single phase of a crystalline material having a high critical temperature, comprising the steps of:
- preparing a starting material of a chemical or mechanical mixture having a composition to produce a compound of Bi.sub.2 Sr.sub.2 Ca.sub.4-x Cu.sub.5-y O.sub.z wherein O.ltoreq.x=1, 0.ltoreq.y.ltoreq.1 and z is adequate to complete conventional oxidation;
- forming an amorphous solid phase by melting said starting material to form a molten mixture and rapidly quenching said molten mixture;
- and
- heat treating said amorphous solid phase at temperatures and times selected from the group consisting of temperature of about 870.degree. C. with time at least about 7-10 days and temperatures more than about 870.degree. C. with times less than about 7-10 days, each of said times and temperatures chosen in the time-temperature-transformation diagrams causing transformation from said amorphous phase to said substantially single phase of crystalline material exhibiting a T.sub.c of about 110.degree. K. as determined by the measurement of substantially zero resistivity for said superconductor.
A high critical temperature superconductor made by the method of claim comprising a substantially single phase structure of Bi.sub.2 Sr.sub.2 Ca.sub.4-x Cu.sub.5-y O.sub.z wherein 0.ltoreq.x.ltoreq.1, 0.ltoreq.y.ltoreq.1, and z the appropriate conventional value to complete adequate conventional oxidation, said single phase structure exhibiting substantially one critical temperature as determined by Magnetization Shielding Effect measurements on said superconductor and said critical temperature being about 110.degree. K. as determined by the measurement of substantially zero resistivity.
A method of treating a high critical temperature superconductor having various different critical temperatures, comprising the steps of:
- preparing a starting crystalline superconductor having a critical temperature of about 110.degree. K. and selected from the group consisting essentially of Bi.sub.2 Sr.sub.2 Ca.sub.4-x Cu.sub.5-y O.sub.z wherein O.ltoreq.x.ltoreq.1, O.ltoreq.y, 1 and z is the appropriate range of conventional value to complete oxidation depending on x and y by the method of claim 14;
- annealing said starting crystalline superconductor at a temperature of about 870.degree. C. and for a time period sufficient to cause at least partial transformation to a second phase having a second critical temperature of about 85.degree. K.;
- and
- annealing at about 870.degree. C. and for said sufficient time period said second superconductor phase having said second critical temperature and transforming said second superconductor phase to reestablish said first superconductor phase having said first critical temperature superconductor phase.
Dependencies are inferred from the claim text.