Enhancing absorption rates of superabsorbents by incorporating a blowing agent
AssigneeNalco Chemical Company
InventorEric J. Lind
Life of this patent
Estimating the term…
Abstract
An improved superabsorbent polymer having increased rate of water absorption is obtained by the addition, preferably prior to polymerization, of a carbonate blowing agent to a monomer solution of the monomers used to form the superabsorbent polymer. Preferred monomers include (meth)acrylic acids, preferably partially neutralized prior to polymerization and appropriate cross-linking agents. The carbonate cross-linking agents are any carbonate salt soluble or dispersible in the monomer solution, prior to polymerization. The multi-valent cationic salts of carbonate are preferred, especially the complex carbonates, for example, of magnesium.
Claims3
A method of improving the rate of absorption of aqueous body fluids, including blood and urine, by (meth)acrylic acid based superabsorbent polymers, which comprises:
- 1). Dissolving at least one (meth)acrylic acid monomer and/or its sodium salt and a cross-linking agent in an aqueous solution to form a monomer solution;
- 2). Adding to the monomer solution a carbonate blowing agent in sufficient amount to form, when polymerized to a hydrogel, a microcellular expanded polymer gel;
- thereby forming a carbonated monomer solution;
- then;
- 3). Initiating free radical polymerization by adding to the carbonated monomer solution either immediately before or immediately after, or simultaneously with the addition of the blowing agent, an effective amount of at least one free radical initiator and polymerizing at temperatures ranging from about 0.degree. C. to about 100.degree. C. to form a microcellular hydrogel;
- and then;
- 4). Chopping or grinding said microcellular hydrogel into gel pieces having a particle diameter size ranging from about 0.1 mm to about 5.0 cm, and then;
- 5). Drying said gel pieces at temperatures ranging from about 85.degree. C.-210.degree. C. to form dry pieces which dry pieces are ground to a size of from 0.05 mm to 5.0 mm diameter to form an improved dry superabsorbent polymer;
- and then;
- 6). Exposing said improved dry superabsorbent polymers to aqueous body fluids, thereby achieving an improved rate of absorption of aqueous body fluids by (meth)acrylic acid based superabsorbents.