Clay slurry
AssigneeH. C. Spinks Clay Company Inc.
InventorWilliam Kohut
Life of this patent
Estimating the term…
Abstract
A slurry composition which may be used to produce a casting slip is provided. The slurry is made by blending a ball clay/water mixture together with a separate mixture of clay and water. The blended slurry thus produced contains from about 0.01 to about 1.0 weight percent of polyelectrolyte. When this blended slurry is mixed with from 40 to 55 parts of nonplastic material (such as flint), a casting slip is produced.
Claims6
A clay/water slurry comprised of from about 55 to about 95 weight percent of kaolinite, from about 5 to about 30 weight percent of quartz, less than about 8 weight percent of montmorillonite, and from about 0.5 to about 8 weight percent of mica, all weights calculated by dry weight of dry clay in the slurry wherein:
- (a) the ratio of the weight of said kaolinite to said montmorillonite in said slurry is at least about 11.0;
- (b) the ratio of the weight of said kaolinite to said mica in said slurry is at least about 8.5;
- (c) the ratio of the weight of said kaolinite to said quartz in said slurry is at least about 3.0;
- (d) said slurry contains from about 58 to about 72 percent (by total weight of slurry) of clay (dry weight);
- (e) said slurry has an initial Brookfield 100 r.p.m. viscosity of from about 90 to about 1,300 centipoise;
- (f) from about 25 to about 50 percent (by weight of dry clay) of the particles in said clay slurry are smaller than about 0.5 microns, from about 50 to about 80 percent of the clay slurry particles are smaller than about 2.0 microns, and from about 70 to about 95 percent of the clay slurry particles are smaller than about 5.0 microns;
- (g) said clay slurry has a specific surface area of from about 16 to about 30 square meters per gram;
- (h) said clay slurry, when freshly made, has a five-minute gel viscosity at 0.5 revolutions per minute of from about 320 to about 26,000 centipoise;
- (i) said clay slurry, when freshly made, has a ten-minute gel viscosity at 0.5 revolutions per minute of from about 320 to about 26,000 centipoise;
- (j) said clay slurry, when freshly made, has a twenty-minute gel viscosity at 0.5 revolutions per minute of from about 320 to about 26,000 centipoise;
- (k) the difference between the twenty-minute gel viscosity of the slurry and its ten-minute gel viscosity is less than about 3,000 centipoise;
- (l) the difference between the twenty-minute gel viscosity of the slurry and its five-minute gel viscosity is less than about 4,000 centipoise;
- (m) said slurry is comprised of from about 0.01 to about 1.0 percent of organic polyelectrolyte (weight of active ingredient, by weight of dry clay in the slurry), wherein said organic polyelectrolyte has a molecular weight of from about 1,400 to about 6,000;
- (n) said slurry is comprised of from about 1 to about 650 parts per million (by dry weight of clay) of soluble sulfate ion;
- (o) said slurry has a settling index of at least about 0.9;
- (p) said slurry has a flow index of from about 20 to about 30 seconds;
- (q) said slurry has a casting rate of from about 30 to about 200 grams at 90 p.s.i. for one hour;
- (r) said slurry has a dry modulus of from about 200 to about 800 pounds per square inch;
- (s) said slurry contains from about 45 to about 70 percent (by weight of dry clay) of silica and from about 20 to about 45 weight percent (by weight of dry clay) of alumina;
- and
- (t) the silica/alumina weight ratio in said clay slurry is from about 1.0 to about 3.5.