Method of making polarization retaining fiber with an elliptical core, with collapsed apertures
AssigneeCorning Incorporated
InventorsGeorge E. Berkey, Robert M. Hawk, Steven H. Tarcza
Life of this patent
Estimating the term…
Abstract
Disclosed is a method of making a polarization retaining single-mode optical fiber. There is initially formed a draw blank having diametrically opposed longitudinal apertures in the cladding glass parallel to the core glass region. The draw blank is drawn into a fiber under such conditions that the apertures close as the fiber is being drawn. The flow of surrounding glass, including the core glass region, toward the collapsing apertures, causes the core to assume an elliptical shape. The apertures are of such cross-sectional area and spacing from the core that the core develops the desired aspect ratio.
Claims17
A method of making a polarization retaining single-mode optical fiber comprising drawing an optical fiber from a cylindrically-shaped draw blank having a cylindrically-shaped glass core surrounded by cladding glass and having apertures consisting of a single pair of cylindrical apertures that are parallel to and diametrically opposed with respect to said core, said fiber being drawn at such a rate that said apertures close, thus causing the core of said fiber to have an elliptical cross-section.
A method of making a polarization retaining single-mode optical fiber comprising the steps of
- forming longitudinal grooves on diametrically opposed sides of a cylindrically-shaped core preform having a glass core surrounded by cladding glass,
- inserting said core preform into a glass tube,
- shrinking said tube onto said core preform,
- fusing the interface between said core preform and said tube, thereby forming a consolidated assembly having longitudinal apertures that are parallel to said core to form a draw blank, and
- drawing an optical fiber from the resultant draw blank at such a rate that said apertures close, thus causing the core of said optical fiber to have an elliptical cross-section.
A method of making a polarization retaining single-mode optical fiber comprising the steps of
- forming longitudinal grooves on diametrically opposed sides of a cylindrically-shaped core preform having a glass core surrounded by cladding glass,
- depositing glass particles on the outer surface of a glass tube,
- inserting said core preform into said glass tube to form an assembly,
- heating said assembly to consolidate said particles, thereby exerting on said tube a radially inwardly directed force that causes said heated tube to shrink onto and fuse to said core preform, thereby forming a consolidated assembly having longitudinal apertures that are parallel to said core to form a draw blank, and
- drawing an optical fiber from the draw blank at such a rate that said apertures close, thus causing the core of said optical fiber to have an elliptical cross-section.
A method of making a polarization retaining single-mode optical fiber comprising drawing an optical fiber from a cylindrically-shaped draw blank having a cylindrically-shaped glass core surrounded by cladding glass and having apertures that are parallel to and diametrically opposed with respect to said core, said fiber being drawn at such a rate that said apertures close, thus causing the core of said fiber to have an elliptical cross-section, said draw blank being formed by the following steps:
- forming longitudinal grooves on diametrically opposed sides of a cylindrically-shaped core preform in which said glass core is surrounded by said cladding glass,
- inserting said core preform into a glass tube to form an assembly having enclosed grooves on diametrically opposed sides of said core, said tube having outer and inner surfaces,
- shrinking said tube onto said core preform to form said apertures,
- fusing said core preform to said tube, thereby forming a consolidated assembly containing said apertures,
- applying a pressure differential across said tube during the steps of shrinking and fusing, whereby the pressure on the outer tube surface exceeds that on the inner tube surface, the pressure differential across said tube being sufficient to collapse said tube onto said core preform, but being insufficient to cause glass to flow into and eliminate said grooves, the step of applying a pressure differential across said tube comprising depositing glass particles on the outer surface of said tube, heating the resultant assembly to consolidate said particles, the process of consolidating said particles exerting a force radially inwardly on said tube, thereby causing said tube to shrink onto said core preform, the step of heating also fusing said tube to said core preform.
Dependencies are inferred from the claim text.