Gunning composition
AssigneeMagneco/Metrel, Inc.
InventorSubrata Banerjee
Life of this patent
Estimating the term…
Abstract
An improved gunning composition for use in the steel industry includes between 60-75% by weight of a refractory base material, 10-20% by weight of silicon carbide, 7-15% by weight of ball clay, 4-8% by weight of a silica binder material, and, optionally, 5-10% by weight of a graphite material. The silica binder replaces binders composed of petroleum pitch or clay. The silica binder causes the composition to have (1) better adhesion, (2) less cracking, (3) improved strength, and (4) increased resistance to oxidation, corrosion and erosion.
Claims13
A gunning composition for repairing and maintaining equipment used for containing and processing molten steel, consisting essentially of:
- at least about 60 weight percent of a refractory base material selected from the group consisting of calcined clay, mullite, brown fused alumina, tabular alumina and combinations thereof;
- greater than 10 to not more than 20 weight percent silicon carbide;
- about 7 to about 15 weight percent ball clay;
- about 5 to about 8 weight percent silicon metal;
- greater than 5 to not more than 10 weight percent graphite;
- and
- about 4 to about 8 weight percent of a binder formed from 15-70 weight percent colloidal silica in an aqueous medium, the colloidal silica having an average diameter of 4-100 millimicrons.
A gunning composition for repairing and maintaining equipment used for containing and processing molten steel, consisting essentially of:
- at least about 60 weight percent calcined clay;
- greater than 10 to not more than 20 weight percent silicon carbide;
- about 7 to about 15 weight percent ball clay;
- about 5 to about 8 weight percent silicon metal;
- greater than 5 to not more than 10 weight percent graphite;
- and
- about 4 to about 8 weight percent of a binder formed from 15-70 weight percent colloidal silica in an aqueous medium, the colloidal silica having an average diameter of 4-100 millimicrons.
A gunning composition for repairing and maintaining equipment used for containing and processing molten steel, consisting essentially of:
- about 60 to about 65 weight percent mullite;
- about 10 to about 20 weight percent silicon carbide;
- about 7 to about 15 weight percent ball clay;
- about 5 to about 8 weight percent silicon metal;
- about 5 to about 10 weight percent graphite;
- and
- about 4 to about 8 weight percent of a binder formed from 15-70 weight percent colloidal silica in an aqueous medium, the colloidal silica having an average diameter of 4-100 millimicrons.
A gunning composition for repairing and maintaining equipment used for containing and processing molten steel, consisting essentially of:
- at least about 60 weight percent brown fused alumina;
- greater than 10 to not more than 20 weight percent silicon carbide;
- about 7 to about 15 weight percent ball clay;
- about 5 to about 8 weight percent silicon metal;
- greater than 5 to not more than 10 weight percent graphite;
- and
- about 4 to about 8 weight percent of a binder formed from 15-70 weight percent colloidal silica in an aqueous medium, the colloidal silica having an average diameter of 4-100 millimicrons.
The gunning composition for repairing and maintaining equipment used for containing and processing molten steel, consisting essentially of:
- at least about 60 weight percent tabular alumina;
- greater than 10 to not more than 20 weight percent silicon carbide;
- about 7 to about 15 weight percent ball clay;
- about 5 to about 8 weight percent silicon metal;
- greater than 5 to not more than 10 weight percent graphite;
- and
- about 4 to about 8 weight percent of a binder formed from 15-70 weight percent colloidal silica in an aqueous medium, the colloidal silica having an average diameter of 4-100 millimicrons.
Dependencies are inferred from the claim text.