Continuous process for removing unstable components from crude oxymethylene copolymer

A continuous process for removing unstable components from crude catalytically prepared oxymethylene copolymer that still contains polymerization catalyst, monomeric starting materials and unstable components, which process comprises preparing said crude copolymer as a solid by bulk catalytic polymerization of trioxane with comonomers in a polymerization unit at a temperature above 65.degree. C., discharging the crude polymerizate, separating the resulting crude solid copolymer and trioxane/formaldehyde gases from one another immediately after leaving the polymerization unit, immediately melting in a pressure zone the crude solid copolymer leaving the polymerization unit without interim storage and in the absence of any material which deactivates the polymerization catalyst, treating the melted copolymer with a catalyst deactivator composition under pressure in at least one subsequent pressure zone, removing volatile components in at least one pressure-release zone in the presence or absence of a co-polymer stabilizer, and discharging the degassed copolymer, the copolymer melt being kept at a temperature above its melting point up to a maximum of 260.degree. C.

A continuous process for removing unstable components from crude solid oxymethylene copolymer prepared by polymerization of trioxane with at least one comonomer at a temperature above 65.degree. C. in a polymerization unit, which copolymer still contains catalysts, monomeric starting materials and unstable components, which process comprises separating the resulting solid crude copolymer and trioxane/formaldehyde gases from one another immediately after leaving the polymerization unit, the gaseous component is fed to a separate treatment stage, the crude copolymer is fully melted in a first pressure zone, in the absence of catalyst deactivator and auxiliary agent, immediately after completion of the polymerization step, the deactivator is subsequently incorporated, alone or together with an auxiliary, under pressure into the resultant copolymer melt in at least one subsequent pressure zone, removing volatile components from the melted copolymer in a pressure-release zone in the presence or absence of a stabilizer, the copolymer melt is kept at a temperature above its melting point up to a maximum of 260.degree. C., and the melting, deactivation and thermal treatment are carried out in a single- or multi-screw extruder or in a disk reactor.

A continuous process for removing unstable components from crude solid oxymethylene copolymer produced by the polymerization of trioxane monomer with at least one comonomer in the presence of a catalyst in a polymerization unit, said process comprising separating the crude solid copolymer from any unreacted monomer and by-products immediately after removing said copolymer from the polymerization unit, transporting said removed copolymer into a melt unit where it is melted into the liquid phase, in the absence of any material which deactivates the polymerization catalyst, and subsequently adding to the melted copolymer a basic deactivator for the polymerization catalyst.

A continuous process for removing unstable components from crude solid oxymethylene copolymer produced by the polymerization of trioxane monomer with at least one comonomer in the presence of a catalyst in a polymerization unit, said process comprising separating the crude solid copolymer from any unreacted monomer and by-products immediately after removing said copolymer from the polymerization unit, transporting said removed copolymer into a melt unit where it is melted into the liquid phase, in the absence of any material which deactivates the polymerization catalyst, and subsequently adding to the melted copolymer an organic deactivator for the polymerization catalyst in an amount from 20 to 5000 ppm relative to the amount of crude oxymethylene copolymer.

A continuous process for removing unstable components from crude solid oxymethylene copolymer produced by the polymerization of trioxane monomer with at least one comonomer in the presence of a catalyst in a polymerization unit, said process comprising separating the crude solid copolymer from any unreacted monomer and by-products immediately after removing said copolymer from the polymerization unit, transporting said removed copolymer into a melt unit where it is melted into the liquid phase, in the absence of any material which deactivates the polymerization catalyst, and subsequently adding to the melted copolymer an inorganic deactivator for the polymerization catalyst in an amount from 1 to 100 ppm relative to the amount of crude oxymethylene copolymer.

A continuous process for removing unstable components from crude solid oxymethylene copolymer produced by the polymerization of trioxane monomer with at least one comonomer in the presence of a catalyst in a polymerization unit, said process comprising separating the crude solid copolymer from any unreacted monomer and by-products immediately after removing said copolymer from the polymerization unit, transporting said removed copolymer into a melt unit where it is melted into the liquid phase in the absence of any material which deactivates the polymerization catalyst, and subsequently adding to the melted copolymer a deactivator for the polymerization catalyst and an auxiliary agent for removing the copolymer from the associated ingredients.

A continuous process for removing unstable components from crude solid oxymethylene copolymer produced by the polymerization of trioxane monomer with at least one comonomer in the presence of a catalyst in a polymerization unit, said process comprising separating the crude solid copolymer from any unreacted monomer and by-products immediately after removing said copolymer from the polymerization unit, transporting said removed copolymer into a melt unit where it is melted into the liquid phase in the absence of any material which deactivates the polymerization catalyst, subsequently adding to the melted copolymer, a deactivator for the polymerization and further treating the copolymer melt at a pressure between 0.001 bar and atmospheric pressure to remove volatile degradation products.