Method for joining ceramic shapes
AssigneeThe United States of America as represented by the United States Department of Energy
InventorBarry H. Rabin
Life of this patent
Estimating the term…
Abstract
A method for joining shapes of ceramic materials together to form a unitary ceramic structure. In the method of the invention, a mixture of two or more chemical components which will react exothermically is placed between the surfaces to be joined, and the joined shapes heated to a temperature sufficient to initiate the exothermic reaction forming a joining material which acts to bond the shapes together. Reaction materials are chosen which will react exothermically at temperatures below the degradation temperature of the materials to be joined. The process is particularly suited for joining composite materials of the silicon carbide-silicon carbide fiber type.
Claims10
A method for joining two or more ceramic shapes to form a unitary ceramic structure comprising:
- providing a joining surface on each ceramic shape to be joined;
- applying a layer of precursor joining mixture to at least one joining surface, said joining mixture being a stoichiometric mixture which when heated to initiation temperature, will react exothermically to form a joining material, said joining mixture being selected from the group consisting of molybdenum and silicon, titanium and carbon, and titanium and boron;
- mating the joining surfaces to be jointed with the joining mixture therebetween;
- pressing the joining surfaces together;
- and
- heating the shapes to initiation temperature whereby the joining mixture reacts exothermically to form the joining material between the joining surfaces which joins the shapes thereby forming a unitary ceramic structure.
A method for joining two or more ceramic shapes of silicon carbide composite material containing silicon carbide fibers to form a unitary ceramic structure comprising:
- providing a joining surface on each ceramic shape to be joined;
- applying a layer of a precursor joining mixture to at least one joining surface, said joining mixture being a stoichiometric mixture which when heated to initiation temperature, will react exothermically to form a joining material, said joining mixture being selected from the group consisting of molybdenum and silicon, titanium and carbon, and titanium and boron;
- mating the joining surfaces to be joined with the joining mixture therebetween;
- pressing the joining surfaces together at a pressure of from about 5 to 50 MPa;
- and
- heating the shapes in an inert atmosphere to initiation temperature whereby the joining mixture reacts exothermically to form the joining material between the joining surfaces which bonds the shapes thereby forming a unitary ceramic structure of silicon carbide composite material containing silicon carbide fibers.
Dependencies are inferred from the claim text.