Shape memory Transparent body and method of using the same
AssigneeMitsubishi Jukogyo Kabushiki Kaisha
InventorsShunichi Hayashi, Yoshiaki Wakita
Life of this patent
Estimating the term…
Abstract
A shape memory transparent body formed from a shape memory transparent polymer having a glass transition point higher than the temperature at which the transparent body is used, said transparent body remembering a basic shape, taking on a second shape upon heating to a temperature higher than the glass transition point and subsequent cooling to a temperature lower than the glass transition point, with the transparent body kept deformed by an external force for the setting of the deformed shape, and restoring the basic shape upon heating to a temperature higher than the glass transition point; and a method of using the shape memory transparent body.
Claims12
A shape memory transparent body of a shape memory transparent polyurethane polymer formed from a bifunctional isocyanate, a bifunctional polyol, and a bifunctional chain extender containing an active hydrogen group, the molecular ratios of each of the components being 2.00-1.10:1.00:1.00-0.10 and having a glass transition point higher than the temperature at which the transparent body is used and a crystallinity of no more than about 2.5 wt %, said transparent body remembering a basic shape, said body prepared by:
- a) forming the polymer into a first shape;
- b) heating said shaped body to a temperature higher than the glass transition point;
- c) cooling the heated body to a temperature lower than the glass transition point of the polymer;
- d) shaping said transparent body into a second shape;
- and then,
- e) heating the body from step d) at a temperature higher than the glass transition point of the polymer to restore the body to the first shape.
A shape memory transparent body of a shape memory transparent urethane polymer formed from a bifunctional isocyanate, a bifunctional polyol, and a bifunctional chain extender containing an active hydrogen group, the molecular ratios of each of the components being 2.00-1.10:1.00:1.00-0.10, the crystallinity of the polymer being no more than about 2.5 weight percent and said polymer having a visible ray penetration of at least 60%, the polymer exhibiting a rubbery state at a temperature less than the glass transition point, a glassy state at a temperature greater than the glass transition point, and being capable of remembering a first shape after being heated to a temperature above the glass transition point and formed into a second shape different from the first shape and cooled below the glass transition point while being maintained in the second shape so that upon heating to a temperature above the glass transition point, the polymer resumes the first shape.