Method for reactivating catalysts used in catalytic vapor phase process for producing dihydrocarbyl carbonates
AssigneeThe Dow Chemical Company
InventorGerald L. Curnutt
Life of this patent
Estimating the term…
Abstract
A process for the preparation of dihydrocarbyl carbonates comprising contacting an alkanol such as methanol, carbon monoxide and oxygen with a heterogeneous catalyst which comprises a metal halide such as cupric chloride or a mixed metal halide such as cupric chloride/potassium chloride impregnated on an appropriate support such as activated carbon; and a process for reactivating metal halide catalysts supported on porous carrier materials comprising drying and then contacting the supported catalysts with a gaseous stream of hydrogen halide for a period of time which is sufficient to convert all of the metal present in whatever form to the corresponding metal halide.
Claims12
A process for reactivating supported heterogeneous metal halide or mixed metal halide catalysts, which have been deactivated in a vapor phase process for carbonylating alkanols to produce dihydrocarbyl carbonates comprising contacting oxygen, carbon monoxide and an alkanol in the presence of the catalyst, comprising drying, and then contacting the supported catalyst with a gaseous stream of hydrogen halide diluted with inert gas or air or mixtures thereof for a period of time which is sufficient to convert essentially all of the metal present in whatever form to the corresponding metal halide.
A process for reactivating an activated carbon-supported cupric chloride catalyst which has been deactivated in a vapor phase process for carbonylating alkanols to produce dihydrocarbyl carbonates comprising contacting oxygen, carbon monoxide and an alkanol in the presence of the catalyst, comprising
- (1) heating the supported catalyst to 125.degree. C. in the presence of a 125 cc (STP) per minute flow of nitrogen,
- (2) holding the catalyst at 125.degree. C. in the presence of the nitrogen for about 2 hours,
- (3) passing a mixture of 10 percent hydrogen chloride/90 percent air at a flow rate of 175 cc (STP) per minute over the catalyst for about 3 hours, and
- (4) cooling the catalyst to room temperature while maintaining the hydrogen chloride/air flow.
A process for reactivating an activated carbon-supported cupric chloride/potassium chloride catalyst, which has been deactivated in a vapor phase process for carbonylating alkanols to produce dihydrocarbyl carbonates comprising contacting oxygen, carbon monoxide and an alkanol in the presence of the catalysts, comprising
- (1) heating the supported catalyst to 125.degree. C. in the presence of a 125 cc (STP) per minute flow of nitrogen,
- (2) holding the catalyst at 125.degree. C. in the presence of the nitrogen for about 2 hours,
- (3) passing a mixture of 10 percent hydrogen chloride/90 percent air at a flow rate of 175 cc (STP) per minute over the catalyst for about 3 hours, and
- (4) cooling the catalyst to room temperature while maintaining the hydrogen chloride/air flow.