High strength structural perlite concrete
AssigneeAdvanced Concrete Technology, Inc.
InventorsDavid A. Smetana, R. Steve Williams
Life of this patent
Estimating the term…
Abstract
A high strength concrete particularly useful for precast, prestressed products comprising by weight of the wet concrete mix, 8 to 60 percent cement, 0.5 to 20 percent smooth-surfaced, vesicular, expanded perlite, 5 to 30 percent water, 0 to 12 percent pozzolan, and fine aggregate and coarse aggregate as appropriate and available in the circumstances. The concrete provides superior bond to reinforcing strands. The smooth-surfaced, vesicular, expanded perlite is unique and novel.
Claims21
A high strength wet mix concrete composition comprising by weight from about
- 8 to 65 percent cement,
- 0.5 to 20 percent smooth-surfaced, vesicular, expanded perlite, at least about 78 percent by weight of which passes through a U.S. Standard Sieve No. 30 (0.6 mm) and at least about 45 percent by weight of which is retained on a U.S. Standard Sieve No. 50 (0.3 mm),
- 5 to 30 percent water,
- 0 to 12 percent finely divided pozzolan,
- 0 to 70 percent fine aggregate,
- 0 to 60 percent coarse aggregate, said concrete composition, after 28 days, having a compressive strength of at least 2000 psi (14 MPa) and an oven dry density of from about 58 to 135 pounds per cubic foot (928 to 2160 kilograms per cubic meter).
A high strength, concrete product cast from a wet concrete mix which is reinforced with steel strands, comprising by weight:
- 10 to 50 percent cement,
- 0.5 to 15 percent smooth-surfaced, vesicular, expanded perlite, at least about 78 percent by weight of which passes through a U.S. Standard Sieve No. 30 (0.6 mm) and at least about 45 percent by weight of which is retained on a U.S. Standard Sieve No. 50 (0.3 mm),
- 5to 25 percent water,
- 0.3 to 10 percent finely divided pozzolan,
- 10 to 70 percent fine aggregate,
- 0 to 50 percent coarse aggregate, said concrete product, after 28 days, having a compressive strength of at least 4000 psi (27 MPa).
A smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), and at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm).
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm), and two to fifteen parts by weight of a pozzolan.
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm), two to ten parts by weight of water, and two to fifteen parts by weight of a pozzolan.
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm), two to fifteen parts by weight of a pozzolan, and ten to fifty parts by weight of a lightweight aggregate.
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm), two to fifteen parts by weight of water, two to fifteen parts by weight of a pozzolan, and ten to fifty parts by weight of lightweight aggregate.
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm), and at least one-half part by weight of a surface active agent.
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm) and from two to fifteen parts by weight of pozzolan which comprises a mixture of diatomaceous earth and undensified microsilica in the proportions of one to four parts by weight of microsilica for each part of diatomaceous earth.
A mixture of ten parts by weight of a smooth-surfaced, vesicular, expanded perlite having an uncompacted bulk density of from 48 to 320 kilograms per cubic meter, at least about 78 percent by weight passing through a U.S. Standard Sieve No. 30 (0.6 mm), at least about 45 percent by weight being retained on a U.S. Standard Sieve No. 50 (0.3 mm), at least about 90 percent by weight being retained on a U.S. Standard Sieve No. 100 (0.15 mm) and from two to fifteen parts by weight of pozzolan which comprises fly ash and a mixture of diatomaceous earth and undensified microsilica in the proportions of one to four parts by weight of microsilica for each part of diatomaceous earth.
Dependencies are inferred from the claim text.