Method for heat processing of silicon
AssigneeShin-Etsu Handotai Co., Ltd.
InventorsIzumi Fusegawa, Hirotoshi Yamagishi, Takao Abe
Life of this patent
Estimating the term…
Abstract
In a method for heat process of silicon, a single crystal silicon produced by the Czochralski process is thermally processed at a low temperature ranging from 400.degree. C. to 550.degree. C. Outside this temperature range, the oxygen precipitate is not adequate. The result is that a predetermined oxygen precipitate can be obtained uniformly in the crystal growth direction without any reduction especially at the crystal bottom part. The resulting silicon is particularly suitable for manufacture of LSI.
Claims11
In a method for substantially uniformly precipitating oxygen throughout a single crystal or silicon which comprises pulling a single crystal of silicon by the Czochralski process, and then heat treating such crystal at an elevated temperature for a time sufficient to cause oxygen to precipitate in said crystal;
- the improvement which comprises, prior to said oxygen precipitation heat treatment, heat treating said single crystal at a high temperature ranging from 1200.degree. to 1350.degree. C. under conditions sufficient to initialize the heat history of said crystal during growing thereof;
- then heat treating said initialized single crystal at a temperature of about 400.degree. to 500.degree. C. for a time sufficient to cause oxygen precipitation nuclei to form substantially uniformly in said single crystal, and then carrying out said oxygen precipitation heat treatment at a temperature which is higher than said oxygen nuclei precipitation heat treating temperature.
A method for heating treating a single crystal of silicon comprising thermally treating such at a high temperature ranging from 1200.degree. to 1350.degree. C. under conditions sufficient to initialize the heat history of said crystal during growing thereof;
- then heat treating said initialized single crystal at a low temperature ranging from 400.degree. C. to 550.degree. C., sufficient to introduce oxygen precipitation nuclei into said single crystal, in the furnace of a Czochralski crystal puller, as an after-heating step, after completion of pulling-up of the said single crystal silicon and then subjecting said heat treated crystal to a higher temperature sufficient to precipitate oxygen at said nuclei.
A method for oxygen precipitate growth control heat processing of silicon, comprising thermally treating a single crystal silicon produced by the Czochralski process at a high temperature ranging from 1,200.degree. C. to 1,300.degree. C. under conditions sufficient to initialize the heat history of said crystal during growing thereof, then thermally processing such crystal at a low temperature ranging from 400.degree. C. to less than 550.degree. C. under conditions sufficient to introduce oxygen precipitation nuclei into said single crystal, and thereafter effecting an oxygen precipitation heat process.
Dependencies are inferred from the claim text.