Reinforced aluminum matrix composite
AssigneeAdvanced Composite Materials Corporation
InventorsJ. Andrew Walker, Edgar A. Starke, Jr., Paul W. Niskanen
Life of this patent
Estimating the term…
Abstract
A reinforced aluminum matrix composite having improved toughness and ductility over known composites, without any sacrifice in strength or stiffness. In particular, the invention relates to a reinforced aluminum alloy consisting essentially of copper and magnesium as the principal alloying elements. The alloy may have other soluble alloying elements up to their solubility limits in the base alloy. The alloy may include a small percentage of insoluble metallic elements in amounts which do not adversely affect the sought after improvements in ductility and toughness. The reinforcement may be either a ceramic material, in the form of whiskers, particles, or chopped fibers, or a metal.
Claims18
In a ceramic reinforced aluminum matrix composite having an aluminum alloy matrix reinforced with a ceramic material the improvement comprising an aluminum alloy matrix consisting essentially of aluminum and soluble amounts of copper and magnesium as the principal alloying elements, wherein said soluble amounts of said alloying elements are within the ranges of about 2.0-4.5% copper and about 0.3-1.8% magnesium, and a small percentage of insoluble metallic alloying elements in amounts which do not adversely affect ductility and fracture toughness of the composite, wherein said small percentage of insoluble metallic elements is not greater than 0.2%.
A composite material consisting essentially of an aluminum alloy matrix reinforced with a ceramic material wherein said aluminum alloy matrix consists essentially of 2.0-4.5% copper and 0.3-1.8% magnesium as the principal alloying elements forming a base alloy, other soluble alloying elements in amounts which do not exceed the solubility limits of said other alloying elements in said base alloy, and not greater than 0.2% insoluble metallic elements.
A reinforced aluminum matrix composite consisting essentially of:
- an aluminum alloy matrix consisting essentially of soluble amounts of copper and magnesium as the principal alloying elements, wherein the copper and magnesium are within the ranges of about 2.0-4.5 weight percent copper and about 0.3-1.8 weight percent magnesium, and not greater than 0.2 weight percent of insoluble metallic elements;
- and
- 5-40 volume percent reinforcement of said aluminum alloy matrix.
A reinforced aluminum matrix composite consisting essentially of:
- a matrix of a base aluminum alloy of 2.0-4.5% copper and 0.3-1.8% magnesium as the principal alloying elements;
- other soluble alloying elements in amounts which do not exceed the solubility limits of said other soluble alloying elements in said base alloy;
- not greater than 0.2% insoluble metallic alloying elements;
- and
- reinforcement of said matrix.
Dependencies are inferred from the claim text.