Method of manufacturing dual alloy turbine disks
AssigneeGeneral Electric Company
InventorsDaniel D. Krueger, Michael E. Sauby, Sulekh C. Jain, Bruce P. Bardes
Life of this patent
Estimating the term…
Abstract
An article of manufacture having at least a first and a second part, each part having different mechanical properties, compositions, microstructures or combinations thereof, being joined together using a forging process to yield a substantially defect-free joint region. The article in the form of a turbine disk is particularly suited for use in a gas turbine engine in which the hub or inner portion must be resistant to low cycle fatigue and have high strength, while the rim or outer portion must be resistant to stress rupture failure and creep failure.
Claims25
A method of making an integral article from a plurality of discrete metal parts by forming a joint between said parts, said parts having interface surfaces to be joined, said method comprising the steps of:
- (a) heating said parts to at least the minimum temperature required for superplastic deformation thereof;
- (b) placing said parts into a die of the closed die type with said interface surfaces opposed to each other, said die including at least one cavity of predetermined size for receiving expelled interface material;
- (c) while maintaining said parts at least at said minimum temperature, placing said parts under compression by applying compressive force to said die such that said interface surfaces are urged into contact against one another with a substantial portion of said applied compressive force directed to the contact area between said parts, the magnitude of said applied compressive force being selected to first bring about relative movement of said surfaces accompanied by extensive local deformation of said surfaces and continuing to apply said compressive force to provide continuing relative movement of said surfaces accompanied by extensive local deformation and material flow from the joint region into said cavity;
- and
- (d) maintaining said compressive force until said interface surfaces have been brought into conforming relationship and said joint between said surfaces has been formed and said cavity is filled.
A method of making a dual alloy turbine disk from discrete metal parts by metallurgically joining first and second parts, said first part comprising an alloy having good hold time fatigue crack growth resistance, high creep resistance and high stress rupture resistance, said second part comprising an alloy having high tensile strength and fatigue crack growth resistance, said method comprising the steps of:
- (a) preforming surfaces of each part in a substantially compound frustoconical fashion to approximately conform to one another when brought into contact;
- (b) heating said parts to at least the minimum temperature required for superplastic deformation thereof;
- (c) assembling said parts with said preformed surfaces opposed to each other in a closed die, said die having two die portions forming a chamber therebetween in the shape of the disk, and at least one of said die portions further including at least one cavity of predetermined size located adjacent the region where joining of said opposed surfaces is expected to occur;
- and
- (d) while maintaining said parts at least at said minimum temperature, placing said parts under compression by applying compressive force to said die such that said opposed preformed surfaces are urged into contact against one another with a substantial portion of said applied compressive force directed to the contact area between said parts, the magnitude of said applied compressive force being selected to first bring about relative movement of said surfaces accompanied by extensive local deformation of said surfaces and the metallurgical joining of said opposed surfaces, followed by material flow in said joint region, said continued force application further causing material from said joint region to be expelled into said cavity.
A method of making a dual alloy turbine disk from discrete metal parts by metallurgically joining said parts, said parts including a rim made from an alloy having good hold time fatigue crack growth resistance, high creep resistance, high stress rupture resistance and high hold time fatigue crack growth resistance, and a hub made from an alloy having high tensile strength and good low cycle fatigue crack growth resistance;
- said method comprising the steps of:
- (a) preforming said rim with a predetermined substantially frustoconical, inward-facing internal surface;
- (b) preforming said hub with a predetermined substantially compound frustoconical, outward-facing external surface;
- (c) heating said parts to at least the minimum temperature required for superplastic deformation of said parts;
- (d) placing said rim within a die of the closed die type;
- (e) placing said hub coaxially within said rim such that said preformed surfaces are opposed to one another;
- said die having two die portions forming a chamber therebetween in the shape of the disk, at least one of said die portions further including at least one cavity of predetermined dimensions located adjacent to and coextensive with the region where joining of said frustoconical preformed surfaces is expected to occur;
- and
- (f) while maintaining said parts at least said minimum temperature, placing said parts under compression in said die such that opposed frustoconical preformed surfaces are urged into contact against one another with a substantial portion of the applied force directed to the contact area between said parts, the magnitude of said applied compressive force being selected to first bring about relative movement of said frustoconical surfaces accompanied by extensive local deformation of said surfaces and the metallurgical joining of said opposed surfaces, followed by material flow in said joint region, said force application further causing material from said joint region to be expelled into said cavity.