AssigneeE. I. Du Pont de Nemours and Company
InventorsFrancis G. Gallagher, Cathy J. Hamilton, Raymond F. Tietz
Life of this patent
Estimating the term…
Abstract
The invention provides a novel polyesters, fibers and films, nonwovens from the fibers and disposable products of the polyesters such as diapers. The products are degradable under the conditions typically existing in waste composting processes, have low ingredient costs and yet provide strength and toughness properties adequate for end uses such as in disposable diapers. The polyesters are based upon polyethylene terephthalate copolymerized with a polyethylene glycol and a 5-sulfoisophthalic acid and, if desired, a polyethylene ether such as diethylene glycol.
Claims12
A fiber and film forming polyester consisting essentially of recurring structural units of the formula
- --C(O)--R--C(O)--OGO--
- wherein R is
- about 97 to 99.9 mole % para-phenylene and
- about 0.1 to 2.5 mole % of the sulfonate radical, ##STR4## where M is an alkali metal or alkaline earth metal,
- and wherein G is
- at least about 13% by weight of a radical of a polyalkylene glycol of molecular weight at least about 250, and
- up to about 40 mole % of a polyethylene ether radical selected from the group consisting of --(CH.sub.2).sub.2 --O--(CH.sub.2).sub.2 -- and --(CH.sub.2).sub.2 --O--(CH.sub.2).sub.2 --O--(CH.sub.2).sub.2 --,
- with the remainder being selected from the group consisting of --(CH.sub.2).sub.2 --, --(CH.sub.2).sub.3 -- and --(CH.sub.2).sub.4 --.
A fiber and film forming copolyester consisting essentially of about 60%-98% by weight of the copolyester being recurring structural units (1) of the formula
- --C(O)--R--C(O)--OGO--
- wherein R is
- about 93 to 99.9 mole % para-phenylene
- and about 0.1 to 2.5 mole % of the sulfonate radical ##STR5## where M is an alkali metal or alkaline earth metal,
- and wherein G is
- at least about 13% by weight of a radical of a polyalkylene glycol of molecular weight at least about 250, and
- up to about 40 mole % of a polyethylene ether radical selected from the group consisting of --(CH.sub.2).sub.2 --O--(CH.sub.2).sub.2 -- and --(CH.sub.2).sub.2 --O--(CH.sub.2).sub.2 --O--(CH.sub.2).sub.2 --,
- with the remainder being selected from the group consisting of --(CH.sub.2).sub.2 --, --(CH.sub.2).sub.3 -- and --(CH.sub.2).sub.4 --,
- and about 2% to 40% by weight of the copolyester being structural units (2) of the formula [--C(O)--Q--O--].sub.n, and Q are such that the hydroxy acid HO-13 C(O)--Q--OH and/or the polyhydroxyacid HO[--C(O)--Q--O--].sub.n H has a melting point at least 5.degree. C. lower than its composition temperature.