Composite for filtering hot gas and method of its manufacture
AssigneeIndustrial Filter & Pump Mfg. Co.
InventorsHenry Schmidt, Jr., James F. Zievers, Paul Eggerstedt
Life of this patent
Estimating the term…
Abstract
A composite filter element for filtering hot gasses is made up of a porous ceramic core to which a porous ceramic, thin outer layer is integrally bonded. The outer layer has a mean pore size which is at least several times smaller than the mean pore size of the substrate and the substrate is at least several times thicker than is the outer layer. The outer layer and the substrate are preferably formed of the same material or of two different materials having essentially the same coefficient of thermal expansion.
Claims4
A method of manufacturing a monolithic filter tube having a porous inner cylindrical layer of ceramic bonded to a porous outer cylindrical layer of ceramic having a porosity different from that of said inner layer, an annular external mounting flange at one end and a gas impervious plug at the other end, comprising the steps of
- heating ceramic particles of a size less than said predetermined size to the melting point of said particles,
- propelling the molten particles onto the outer surface of said substrate to form a coating on said substrate, and then
- firing the coated substrate.
A method of manufacturing a monolithic filter tube having a porous inner cylindrical layer of ceramic bonded to a porous outer cylindrical layer of ceramic having a porosity different from that of said inner layer, an annular external mounting flange at one end and a gas impervious plug at the
- forming a tubular substrate of ceramic particles of a predetermined size,
- feeding ceramic particles smaller then said predetermined size into a plasma flame, then
- blowing said ceramic particles from said flame onto said tubular substrate to form a coating on said substrate, and then
- firing the coated substrate.
A method of manufacturing a monolithic filter tube having a porous inner cylindrical layer of ceramic bonded to a porous outer cylindrical layer of ceramic having a porosity different from that of said inner layer, an annular external mounting flange at one end and a gas impervious plug at the other end, comprising the steps of
- forming a tubular substrate of ceramic particles of a predetermined size,
- coating the outer surface of said substrate with a bonding material,
- applying to said coating a mixture of a bonding agent and ceramic particles smaller then said predetermined size to coat said substrate, and
- firing said coated substrate at a temperature greater than the vaporizing temperatures of said bonding agents.
A method of manufacturing a monolithic filter tube having a porous inner cylindrical layer of ceramic bonded to a porous outer cylindrical layer of ceramic having a porosity different from that of said inner layer, an annular external mounting flange at one end and a gas impervious plug at the other end, comprising the steps of
- forming a tubular substrate of ceramic particles of a predetermined size,
- providing a slurry of a liquid, a binder, and ceramic particles of a size less then said predetermined size,
- passing said slurry through said substrate until a layer of said ceramic particles of a size less then said predetermined size is deposited on the surface of said substrate, and then
- firing said substrate and said layer.
Dependencies are inferred from the claim text.