Metallized ceramic substrate and method therefor
OwnerKalman F. Zsambokyinventor
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
OwnerKalman F. Zsambokyinventor
Estimating the term…
A metallized ceramic substrate having an enhanced bond strength between the ceramic substrate and a conductive metal layer bonded thereto is disclosed. The metallized ceramic substrate includes a heterogeneous juncture band between a ceramic workpiece and a layer of electrically conductive material. The metallized ceramic substrate is made by a process which includes an acid etchant step that increases the actual surface area of the treated surface of the ceramic workpiece without undermining the integrity of the ceramic surface while at the same time selectively attacking vitreous binder phase present between substrate grains and creating even deeper penetration at the relatively higher energy triple joint junctures. In this manner, metal anchor sites that enhance adhesion are provided. During subsequent high temperature firing these anchors hold the resulting composite together as a chemical bond is formed in addition to a mechanical bond or interlock.
In a method for the manufacture of a metal-ceramic composite by electroless deposition of a conductive metal layer onto a ceramic substrate, the improvement which comprises the step of acid etching grain boundaries of the working surface of the substrate, prior to electroless deposition of the conductive metal thereon, to a depth equal to at least about the diameter of an average grain at the working surface while maintaining a monolithic working surface of the substrate.
In a method for the manufacture of a copper-alumina composite by electroless deposition of a copper layer into an alumina substrate, the improvement which comprises the step of acid etching vitreous grain boundaries of a working surface of said alumina substrate, prior to electroless deposition of the copper thereon, to a depth equal to at least about the diameter of an average grain at the working surface while maintaining a monolithic working surface of the substrate.
In a method for the manufacture of a metalceramic composite by a sensitizer/activator electroless metal deposition process, the improvement which comprises the steps of (a) acid etching a working surface of said ceramic, (b) contacting the resulting, acid-etched ceramic surface with an alkaline, palladium ion-containing activator solution wherein the palladium ion concentration is less than about 200 parts per million for a time period sufficient to deposit palladium ions thereon, (c) reducing the deposited palladium ions to palladium metal on said surface, (d) depositing by electroless deposition a layer of conductive metal onto said palladium metal-bearing surface, and (e) thereafter firing the produced metal-ceramic composite at a temperature sufficient to melt a portion of the metallic composition present at the interface of the deposited metal layer and the acid-etched surface.
In a method for the manufacture of a metal-ceramic composite by a sensitizer/activator electroless metal deposition process, the improvement which comprises the steps of (a) acid etching a working surface of said ceramic, (b) contacting the resulting, acid-etched ceramic surface with an alkaline, palladium ion-containing activator solution wherein the palladium ion concentration is less than about 200 parts per million for a time period sufficient to deposit palladium ions thereon, (c) reducing the deposited palladium ions to palladium metal on said surface, (d) depositing by electroless deposition a layer of conductive metal onto said palladium metal-bearing surface, (e) depositing by electrolytic deposition additional conductive metal onto said layer of conductive metal deposited by electroless deposition, and (f) thereafter firing the produced metal-ceramic composite at a temperature sufficient to melt a portion of the metallic composition present at the interface of the deposited metal layer and the acid-etched surface.