US 5,041,261 A · Method for manufacturing ceramic-metal articles

Abstract

A method for manufacturing a dense cermet article including about 80-95% by volume of a granular hard phase and about 5-20% by volume of a metal binder phase. The hard phase is (a) the hard refractory carbides, nitrides, carbonitrides, oxycarbides, oxynitrides, carboxynitrides, borides, and mixtures thereof of the elements selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, and B, or (b) the hard refractory carbides, nitrides, carbonitrides, oxycarbides, oxynitrides, and carboxynitrides, and mixtures thereof of a cubic solid solution of Zr--Ti, Hf--Ti, Hf--Zr, V--Ti, Nb--Ti, Ta--Ti, Mo--Ti, W--Ti, W--Hf, W--Nb, or W--Ta. The binder phase is a combination of Ni and Al having a Ni:Al weight ratio of from about 85:15 to about 88:12, and 0-5% by weight of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Co, B, and/or C. The method involves presintering the hard phase/binder phase mixture in a vacuum or inert atmosphere at about 1475.degree.-1675.degree. C., then HIPing at about 1575.degree.-1675.degree. C., in an inert atmosphere, and at about 34-207 MPa pressure. Limiting the presintering temperature to 1475.degree.-1575.degree. C. and keeping the presintering temperature at least 50.degree. C. below the hot pressing temperature, produces an article of gradated hardness, harder at the surface than at the core.

Claims9

Dependent claims

A process for producing a ceramic-metal article comprising the steps of:

presintering, in a vacuum or inert atmosphere at about 1475.degree.-1675.degree. C. and for a time sufficient to permit development of a microstructure with closed porosity, a mixture of about 80-95% by volume of a granular hard phase component consisting essentially of a ceramic material selected from the group consisting of the carbides, nitrides, carbonitrides, oxycarbides, oxynitrides, and carboxynitrides of a cubic solid solution of tungsten and titanium;
and about 5-20% by volume of a metal binder phase component, wherein said binder phase component consists essentially of nickel and aluminum, in a ratio of nickel to aluminum of from about 85:15 to about 88:12 by weight, and 0-5% by weight of an additive selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, boron, carbon, and combinations thereof;
and densifying said presintered mixture by hot isostatic pressing at a temperature of about 1575.degree.-1675.degree. C., in an inert atmosphere, and at about 34-207 MPa pressure for a time sufficient to produce an article having a density of at least about 95% of theoretical.

A process for producing a ceramic-metal article comprising the steps of:

presintering, in a vacuum or inert atmosphere at about 1475.degree.-1675.degree. C. and for a time sufficient to permit development of a microstructure with closed porosity, a mixture of about 80-95% by volume of a granular hard phase component consisting essentially of a ceramic material selected from the group consisting of (a) the hard refractory carbides, nitrides, carbonitrides, oxycarbides, oxynitrides, carboxynitrides, borides, and mixtures thereof of the elements selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, and boron, and (b) the hard refractory carbides, nitrides, carbonitrides, oxycarbides, oxynitrides, and carboxynitrides, and mixtures thereof of a cubic solid solution selected from the group consisting of zirconium-titanium, hafnium-titanium, hafnium-zirconium, vanadium-titanium, niobium-titanium, tantalum-titanium, molybdenum-titanium, tungsten-titanium, tungsten-hafnium, tungsten-niobium, and tungsten-tantalum;
and about 5-20% by volume of a metal binder phase component, wherein said binder phase component consists essentially of nickel and aluminum, in a ratio of nickel to aluminum of from about 85:15 to about 88:12 by weight, and 0-5% by weight of an additive selected from the group consisting of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, boron, carbon, and combinations thereof;
and densifying said presintered mixture by hot isostatic pressing at a temperature of about 1575.degree.-1675.degree. C., in an inert atmosphere, and at about 34-207 MPa pressure for a time sufficient to produce an article having a density of at least about 95% of theoretical.

Dependencies are inferred from the claim text.

Method for manufacturing ceramic-metal articles

Life of this patent

Method for manufacturing ceramic-metal articles

Life of this patent

Abstract

Claims9