Method for making a light metal-rare earth metal alloy
AssigneeAluminum Company of America
InventorsGary P. Tarcy, Perry A. Foster, Jr.
Life of this patent
Estimating the term…
Abstract
A method for making a light metal-rare earth metal alloy comprises adding a pellet to a bath of molten light metal, said pellet consisting essentially of a mixture of light metal powder and rare earth metal-containing compound. Such pellets, which are made under pressures of about 9 ksi or more, are preferably added to molten baths of aluminum, magnesium or combinations thereof. The light metal powders and rare earth metal-containing compounds that are mixed together to form said pellets are preferably substantially similar in terms of median particle size. This method is suitable for aluminothermically reducing scandium oxide to make aluminum-scandium alloy therefrom.
Claims17
A method for making an aluminum-scandium allow which comprises:
- (a) mixing aluminum powder with a finely divided scandium-containing compound;
- (b) forming a pellet from the mixture of aluminum powder and scandium compound;
- and
- (c) feeding the pellet to a molten aluminum bath.
A method for making an aluminum-scandium master alloy which comprises:
- (a) providing a mixture of powdered aluminum and scandium oxide powder, the amount of aluminum exceeding the amount of scandium oxide in said mixture;
- (b) compacting the mixture into a pellet under high pressure at one or more temperatures below about 600.degree. C. (1112.degree. F.);
- (c) making the pellet wettable with molten aluminum;
- (d) adding the pellet to a bath of molten aluminum;
- and
- (d) removing aluminum oxide from the bath.
A method for aluminothermically reducing scandium oxide to form an aluminum-scandium alloy therefrom, said method comprising:
- (a) providing an aluminum powder having a median particle size greater than about 5 microns and less than about 150 microns;
- (b) providing a scandium oxide powder having a median particle size greater than about 5 microns and less than about 150 microns;
- (c) forming a mixture from the aluminum and scandium oxide powders, the molar ratio of aluminum to scandium oxide in said mixture being greater than about 30;
- (d) pelletizing the mixture at a pressure of about 9 ksi or more;
- and
- (e) adding the pelletized mixture to a bath of molten aluminum.
A method for adding scandium to an aluminum alloy which comprises:
- (a) providing an aluminum powder;
- (b) providing scandium oxide with a median particle size close to that of the aluminum powder;
- (c) mixing scandium oxide with a majority of the aluminum powder;
- (d) compressing the scandium oxide- aluminum powder mixture into a pellet under high pressure;
- and
- (e) reacting the pellet with a molten aluminum bath containing up to about 1 wt. % flux.
A method for alloying aluminum and scandium which comprises:
- (a) providing a mixture of powdered aluminum and substantially similarly-sized scandium oxide powder, the molar ratio of aluminum to scandium oxide in said mixture being greater than about 30;
- (b) pelletizing the mixture under high pressure;
- and
- (c) dissolving the pelletized mixture in a bath of wetting molten metal alloy.
Dependencies are inferred from the claim text.