Fiber-containing composite
AssigneeGeneral Electric Company
InventorsMarcus P. Borom, William B. Hillig, Raj N. Singh, William A. Morrison, Leonard V. Interrante
Life of this patent
Estimating the term…
Abstract
Fibrous material is coated with boron nitride and a silicon-wettable material, the coated fibrous material is admixed with an infiltration-promoting material which is at least partly elemental carbon and the mixture is formed into a preform which is infiltrated with molten silicon producing a composite containing boron nitride coated fibrous material.
Claims54
A process for producing a composite with a porosity of less than about 20% by volume comprised of boron nitride-coated fibrous material and a matrix phase, said fibrous material component of said coated fibrous material comprising at least about 5% by volume of the composite, said matrix phase containing silicon carbide formed in situ in an amount of at least about 5% by volume of the composite and elemental silicon in an amount of at least about 1% by volume of the composite, which comprises the following steps:
- (a) depositing boron nitride on a fibrous material producing a coating thereon which leaves no significant portion of said fibrous material exposed, said fibrous material being selected from the group consisting of elemental carbon, a Si-C containing material containing at least about 50% by weight silicon and at least about 25% by weight carbon, and a combination thereof;
- (b) depositing a silicon-wettable material on said boron nitride-coated fibrous material producing a coating thereon which leaves no significant portion of said boron nitride exposed, said silicon-wettable material adhering to boron nitride sufficiently to form said coating thereon and being wetted by silicon sufficiently to produce said composite;
- (c) admixing an infiltration-promoting material containing elemental carbon with the resulting coated fibrous material producing a mixture wherein the fibrous material component of said coated fibrous material comprises at least about 5% by volume of said mixture;
- (d) forming said mixture into a preform having an open porosity ranging from about 25% by volume to about 90% by volume of the preform;
- (e) contacting said preform with silicon-associated infiltrating means whereby said silicon is infiltrated into said preform;
- (f) heating the resulting structure in a partial vacuum to a temperature at which said silicon is molten and infiltrating said molten silicon into said preform to produce an infiltrated product having the composition of said composite, said preform containing sufficient elemental carbon to react with said silicon to form said composite, said partial vacuum being at least sufficient to remove gas from said preform so as to allow said molten silicon to infiltrate said preform;
- and
- (g) cooling said product to produce said composite.
A composite comprised of boron nitride-coated fibrous material and a matrix phase containing silicon carbide phase and elemental silicon phase, said silicon carbide phase being present in an amount of at least about 5% by volume of said composite, said elemental silicon phase being present in an amount of at least about 1% by volume of said composite, said fibrous material component of said boron nitride-coated material being present in an amount of at least about 5% by volume of said composite, said fibrous material component of said coated fibrous material being selected from the group consisting of elemental carbon, a SiC-containing material containing by weight of the SiC-containing material of least about 50% by weight of silicon and at least about 25% by weight of carbon, and a combination thereof, said boron nitride coating being at least detectable by scanning electron microscopy, said composite having a porosity of less than about 20% by volume.
A composite comprised of boron nitride-coated fibrous material and a matrix phase, said fibrous material component of said boron nitride-coated material being present in an amount ranging from about 10% by volume to about 70% by volume of the composite and being selected from the group consisting of elemental carbon, a SiC-containing material containing by weight of the SiC-containing material at least about 50% by weight of silicon and at least about 25% by weight of carbon, and a combination thereof, said boron nitride coating being at least detectable by scanning electron microscopy, said coated fibrous material being distributed through said composite, said matrix phase being comprised of silicon carbide phase and elemental silicon phase, said silicon carbide phase being present in an amount of at least about 10% by volume of said composite, said elemental silicon phase being present in an amount of at least about 1% by volume of said composite, said matrix phase totally enveloping said boron nitride-coated fibrous material, said composite having a porosity of less than about 20% by volume.
A process for producing a composite with a porosity of less than about 5% by volume comprised of boron nitride-coated fibrous material and a matrix phase, said fibrous material component of said coated fibrous material comprising at least about 5% by volume of the composite, said matrix phase containing silicon carbide formed in situ in an amount of at least about 5% by volume of the composite and elemental silicon in an amount of at least about 1% by volume of the composite, which comprises the following steps:
- (a) depositing boron nitride on a fibrous material producing a coating thereon which leaves no significant portion of said fibrous material exposed, said fibrous material being selected from the group consisting of elemental carbon, a substance containing at least about 50% by weight silicon and at least about 25% by weight carbon, and a combination thereof,
- (b) depositing a silicon-wettable material on said boron nitride-coated fibrous material producing a coating thereon which leaves no significant portion of said boron nitride exposed, said silicon-wettable material adhering to boron nitride sufficiently to form said coating thereon and being wetted by silicon sufficiently to produce said composite;
- (c) admixing an infiltration-promoting material containing elemental carbon with the resulting coated fibrous material producing a mixture wherein the fibrous material component of said coated fibrous material comprises at least about 5% by volume of said mixture;
- (d) forming said mixture into a preform having an open porosity ranging from about 35% by volume to about 80% by volume of the preform;
- (e) contacting said preform with silicon-associated infiltrating means whereby said silicon is infiltrated into said preform,
- (f) heating the resulting structure in a partial vacuum to a temperature at which said silicon is molten and infiltrating said molten silicon into said preform to produce an infiltrated product having the composition of said composite, said preform containing sufficient elemental carbon to react with said silicon to form said composite, said partial vacuum being at least sufficient to remove gas from said preform so as to allow said molten silicon to infiltrate said preform;
- and
- (g) cooling said product to produce said composite.
A composite comprised of boron nitride-coated fibrous material and a matrix phase containing silicon carbide phase and elemental silicon phase, said silicon carbide phase being present in an amount of at least about 5% by volume of said composite, said elemental silicon phase being present in an amount of at least about 1% by volume of said composite, said fibrous material component of said boron nitride-coated material being present in an amount of at least about 5% by volume of said composite, said fibrous material component of said coated fibrous material being comprised of silicon carbide, said boron nitride coating being at least detectable by scanning electron microscopy, said composite having a porosity of less than about 20% by volume.
A composite comprised of boron nitride-coated fibrous material and a matrix phase containing silicon carbide phase and elemental silicon phase, said silicon carbide phase being present in an amount of at least about 5% by volume of said composite, said elemental silicon phase being present in an amount of at least about 1% by volume of said composite, said fibrous material component of said boron nitride-coated material being present in an amount of at least about 5% by volume of said composite, said fibrous material component of said coated fibrous material being comprised of elemental carbon, said boron nitride coating being at least detectable by scanning electron microscopy, said composite having a porosity of less than about 20% by volume.
A process for producing a composite with a porosity of less than about 20% by volume comprised of boron nitride-coated fibrous material and a matrix phase, said fibrous material component of said coated fibrous material comprising at least about 5% by volume of the composite, said matrix phase containing silicon carbide formed in situ in an amount of at least about 5% by volume of the composite and elemental silicon in an amount of at least about 1% by volume of the composite, which comprises the following steps:
- (a) depositing boron nitride on a fibrous material producing a coating thereon which leaves no significant portion of said fibrous material exposed, said fibrous material being selected from the group consisting of elemental carbon, a SiC-containing material containing at least about 50% by weight silicon and at least about 25% by weight carbon, and a combination thereof;
- (b) depositing a silicon-wettable material on said boron nitride-coated fibrous material producing a coating thereon which leaves no significant portion of said boron nitride exposed, said silicon-wettable material adhering to boron nitride sufficiently to form said coating thereon and being wetted by silicon sufficiently to produce said composite;
- (c) forming a preform comprised of a mixture of the resulting coated fibrous material and an infiltration promoting material containing elemental carbon wherein the fibrous material component of said coated fibrous material comprises at least about 5% by volume of said mixture, said preform having an open porosity ranging from about 25% by volume to about 90% by volume of the preform;
- (d) contacting said preform with silicon-associated infiltrating means whereby said silicon is infiltrated into said preform;
- (e) heating the resulting structure in a partial vacuum to a temperature at which said silicon is molten and infiltrating said molten silicon into said preform to produce an infiltrated product having the composition of said composite, said preform containing sufficient elemental carbon to react with said silicon to form said composite, said partial vacuum being at least sufficient to remove gas from said preform so as to allow said molten silicon to infiltrate said preform;
- and
- (f) cooling said product to produce said composite.
Dependencies are inferred from the claim text.